The Performance of Phenolic Epoxy Coating after Thermal Exposure for Corrosion Protection in Marine Environments

Picture for The Performance of Phenolic Epoxy Coating after Thermal Exposure for Corrosion Protection in Marine Environments
Available for download

Organic coating is the most widely used method of corrosion protection. its corrosion protective abilities depend on physical, chemical and mechanical properties including adhesion to a substrate and essential barrier properties against corrosive species, such as water and oxygen. The durability of corrosion protection coatings is evaluated based on their effectiveness in providing long-term protection to metallic substrates when these materials are exposed to aggressive corrosion environments.

Product Number: 51323-19046-SG
Author: S. Ahmed, T. Becker, Y. Hou, K. Lepkova, T. Pojtanabuntoeng
Publication Date: 2023
$0.00
$20.00
$20.00

Corrosion protection by a commercial phenolic epoxy coating for carbon steel panels was examined after exposure to a thermal cycling regimen of 22 °C and 120 °C for 40 d. The panels, along with freshly coated samples, were tested and immersed in solutions with 3.5 and 5 wt.% NaCl at 80 °C for 60 d. Some of the samples were also exposed to water condensation. Coating behaviour was investigated by visual observation (degree of blistering and evaluation of degradation) of coating, and electrochemical impedance spectroscopy (EIS). The EIS results, and the degree of blistering and delamination around the scribed regions of the panels suggested that 3.5 wt.% NaCl caused greater degradation than did 5 wt.% NaCl. Thermal exposure improved corrosion protection as evidenced by the higher impedance (>0.1 GΩ cm2) of the specimens, the absence of blisters on the panel surfaces and the reduced delamination around the scribe areas of the thermal cycling panels compared with the freshly coated samples. The results showed that the organic coating exposed to heat exhibited an improved resistance against severe marine conditions.

Corrosion protection by a commercial phenolic epoxy coating for carbon steel panels was examined after exposure to a thermal cycling regimen of 22 °C and 120 °C for 40 d. The panels, along with freshly coated samples, were tested and immersed in solutions with 3.5 and 5 wt.% NaCl at 80 °C for 60 d. Some of the samples were also exposed to water condensation. Coating behaviour was investigated by visual observation (degree of blistering and evaluation of degradation) of coating, and electrochemical impedance spectroscopy (EIS). The EIS results, and the degree of blistering and delamination around the scribed regions of the panels suggested that 3.5 wt.% NaCl caused greater degradation than did 5 wt.% NaCl. Thermal exposure improved corrosion protection as evidenced by the higher impedance (>0.1 GΩ cm2) of the specimens, the absence of blisters on the panel surfaces and the reduced delamination around the scribe areas of the thermal cycling panels compared with the freshly coated samples. The results showed that the organic coating exposed to heat exhibited an improved resistance against severe marine conditions.

Product tags
Also Purchased
Picture for Influence Of Brine Precipitates On Materials Performance In Geothermal Applications
Available for download

Influence Of Brine Precipitates On Materials Performance In Geothermal Applications

Product Number: 51323-18813-SG
Author: Anastasia Stoljarova, Ralph Bäßler, Simona Regenspurg
Publication Date: 2023
$20.00

Since geothermal reservoirs are a feasible energy source to replace fossil fuel supply, many technologies have been developed to take advantage of geothermal energy. Nevertheless, due to the chemical composition of hydrothermal fluids and temperatures, service conditions in geothermal facilities are demanding in many cases in terms of corrosion. Therefore, materials selection based on preliminary material qualification is essential to guarantee a secure and reliable operation of the facilities.
Picture for Weathering Of Industrial Coatings: Correlation Between Three Years Outdoor Florida Exposure And Four Accelerated Weathering Methods
Available for download

Weathering Of Industrial Coatings: Correlation Between Three Years Outdoor Florida Exposure And Four Accelerated Weathering Methods

Product Number: 51323-18869-SG
Author: Sean Fowler, Kurt Wood, David Duecker
Publication Date: 2023
$20.00


Implementation of classification and certification programs for durable industrial and infrastructure maintenance coating systems is hindered by a lack of test protocols to reliably accelerate the aging process and estimate service lifetime. This gap in the industry also hurts development efforts to
reformulate or add new color choices to existing product lines. The first problem can be addressed by performing long-term weathering testing at outdoor exposure sites in places like south Florida and Arizona, but the need to wait 5 or 10 years or longer to confirm a classification or certify a product makes such schemes difficult to implement and ultimately reduces their value.
Picture for Material Selection for anthropogenic CO2 injection: mechanical and corrosion performances of steels under dense CO2 with impurities
Available for download

Material Selection for anthropogenic CO2 injection: mechanical and corrosion performances of steels under dense CO2 with impurities

Product Number: 51323-18886-SG
Author: Cécile Millet, Guillaume Néel, Luciana Lima, Diana Rodriguez Barrera
Publication Date: 2023
$20.00

Carbon capture and storage (CCS) are technologies aimed at capturing CO2, followed by transportation to a storage site and injection into one of several types of stable geological formations, to trap and prevent its subsequent emission. Though CO2 transport and injection for Enhanced Oil Recovery (EOR) are known for over 40 years, new challenges arise when the CO2 source is anthropogenic, meaning with a human-cause origin and not natural (as in EOR). EU Directive 2009/31/EC states that CO2 streams from power stations or industrial plants "shall consist overwhelmingly of CO2" but may contain associated incidental substances (e.g., SOx, NOx, O2, H2S).
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support