Reduction Of Conservatism In SSC Testing For Sour Gas Well Tubulars

Picture for Reduction Of Conservatism In SSC Testing For Sour Gas Well Tubulars
Available for download

Martensitic stainless steel (MSS) well tubulars are favorable due to their high strength and relatively low cost and are therefore widely applied in the Oil & Gas industry. This is especially the case for 13Cr and Super13Cr grades, which are often selected for mildly sour gas fields, where a relatively low content of H2S is present. When selecting martensitic stainless steels for sour service, the susceptibility to Stress Corrosion Cracking (SCC) and Sulfide Stress Cracking (SSC), determined by standard laboratory tests, are the most important selection criteria.

Product Number: 51322-17776-SG
Author: Marc Wilms, Johan Smit, Willem Maarten van Haaften, Sytze Huizinga, Wouter Koot, Daniela Garcia, Harold Evin, Michel Bonis, Hervé Marchebois, Edmund J.F. Dickinson, Gareth Hinds
Publication Date: 2022
Industries: Corrosion Monitoring and Control , Coatings
$0.00
$20.00
$20.00

Due to their high strength and relatively low cost, martensitic stainless steel (MSS) well tubulars are attractive. However, sour applications of MSS are limited by their susceptibility to Sulphide Stress Cracking (SSC) under shut-in conditions, where the pressure is the highest and the temperature the lowest. This currently restricts their use to a greater extent than high temperature pitting and Stress Corrosion Cracking (SCC). 

A comparison between field experience in mildly sour gas wells and laboratory test data on 13Cr MSS tubulars showed that in the laboratory SSC tests, cracking is observed under conditions that are significantly less severe than the field conditions in which these tubulars are operated without reported failures. This raised the question whether the current method of SSC testing is too conservative. To investigate this, a detailed assessment of field-relevant exposure conditions for SSC was carried out.

Susceptibility to SSC requires a near to ambient temperature. Therefore, only the top section of the well can be susceptible, after closing in the well and a subsequent cooling down period. Because the liquids will drain away after closing in a gas well, the tubular will be exposed to a thin water film (or water droplets) only. This thin water film exposure was evaluated and modelled. Results indicate a lower susceptibility to SSC than fully immersed conditions, attributable to pH elevation in the thin water film, which is induced by very slow corrosion under passive conditions. Existing SSC test methods were adapted to simulate the thin water film exposure in a realistic way, which resulted in a new fit-for-purpose SSC test method.

The results obtained with the thin water film test demonstrate that for mildly sour gas wells, the safe operating envelope of martensitic stainless steels can be extended. 

Due to their high strength and relatively low cost, martensitic stainless steel (MSS) well tubulars are attractive. However, sour applications of MSS are limited by their susceptibility to Sulphide Stress Cracking (SSC) under shut-in conditions, where the pressure is the highest and the temperature the lowest. This currently restricts their use to a greater extent than high temperature pitting and Stress Corrosion Cracking (SCC). 

A comparison between field experience in mildly sour gas wells and laboratory test data on 13Cr MSS tubulars showed that in the laboratory SSC tests, cracking is observed under conditions that are significantly less severe than the field conditions in which these tubulars are operated without reported failures. This raised the question whether the current method of SSC testing is too conservative. To investigate this, a detailed assessment of field-relevant exposure conditions for SSC was carried out.

Susceptibility to SSC requires a near to ambient temperature. Therefore, only the top section of the well can be susceptible, after closing in the well and a subsequent cooling down period. Because the liquids will drain away after closing in a gas well, the tubular will be exposed to a thin water film (or water droplets) only. This thin water film exposure was evaluated and modelled. Results indicate a lower susceptibility to SSC than fully immersed conditions, attributable to pH elevation in the thin water film, which is induced by very slow corrosion under passive conditions. Existing SSC test methods were adapted to simulate the thin water film exposure in a realistic way, which resulted in a new fit-for-purpose SSC test method.

The results obtained with the thin water film test demonstrate that for mildly sour gas wells, the safe operating envelope of martensitic stainless steels can be extended. 

Product tags
Also Purchased
Picture for Recent Advances On The Influence Of Microstructural Characteristics On Corrosion Resistance In H2SO4 Of Anodized Titanium
Available for download

Recent Advances On The Influence Of Microstructural Characteristics On Corrosion Resistance In H2SO4 Of Anodized Titanium

Product Number: 51322-17589-SG
Author: Luca Casanova, MariaPia Pedeferri, Gianluigi A. Botton, Marco Ormellese
Publication Date: 2022
$20.00

Industrial usage of Plasma Electrolytic Oxidation (PEO) has grown consistently in recent years, thanks to the improved characteristics imparted to the oxide film in terms of surface adhesion, hardness, crystallinity, uniformity, and corrosion resistance. The metallic substrate is not subjected to elevated temperature and the overall equipment complexity is relatively simple, making the technique a good candidate for surface functionalization. In PEO treatments, high voltages are employed (~ 150-750 V 1) allowing for the formation of an insulating, or at least semiconductive, oxide layer that’s limits ion transport responsible for the initial coating growth. Beyond the spark voltage (prerequisite the enter the PEO regime) oxidation does not occur only as the result of a continuous flow of ions but rather it takes place after the cooling of a plasma discharge.
Picture for Refinement Of Citric Acid Passivation Methods And Comparison To Traditional Nitric Acid Based Chemistries
Available for download

Refinement Of Citric Acid Passivation Methods And Comparison To Traditional Nitric Acid Based Chemistries

Product Number: 51322-17628-SG
Author: David G. Enos, Derek Wichhart
Publication Date: 2022
$20.00

Traditional solutions for the chemical passivation of stainless steel are nitric acid based, with the addition of sodium dichromate as an inhibitor for precipitation hardened and free machining stainless steels. These passivation chemistries are difficult to handle from an environmental health and safety point of view, particularly the dichromate inhibited versions. Citric acid passivation has been pursued as a replacement for both nitric acid and inhibited nitric acid based chemistries for many years, and has been incorporated into consensus specifications such as ASTM A967 and SAE AMS2700.
Picture for Predictive Coating Condition Model For Coating Lifetime Under Environmental Stressors
Available for download

Predictive Coating Condition Model For Coating Lifetime Under Environmental Stressors

Product Number: 51322-17685-SG
Author: Victoria Avance, Brandi Clark, Liam Agnew, Fritz Friedersdorf
Publication Date: 2022
$20.00

The corrosion of aircraft costs the U.S. Department of Defense billions of dollars annually and accounts for a significant portion of maintenance time and costs.1 Coatings are the most effective way to protect aircraft, but they have a finite lifetime and must be maintained or replaced before the underlying substrate is damaged by corrosion. Current aircraft maintenance practices call for coating inspections and maintenance based on elapsed time and not on measurements of coating health. Coating lifetime varies depending on the environmental stressors experienced in service, including temperature, humidity, and salt loading.
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support