Improved Localized Corrosion Models For Stainless Steels In Aqueous Chloride Environments With Low Levels Of Dissolved Oxygen

Improved Localized Corrosion Models for Stainless Steels in Aqueous Chloride Environments with Low Levels of Dissolved Oxygen
Available for download

In Upstream, CRAs (Corrosion Resistant Alloys) are widely selected to handle seawater and brines in piping, valves, pumps, heat exchangers, vessels, and seawater injection1-4. Also, disposal of produced water is commonly performed through injection into spent fields. Water from a variety of sources including produced water, seawater and surface/fresh water may also be injected to create pressure drive for existing fields. Usually dissolved oxygen (DO) is not fully controlled when there are multiple sources of injection water and sometimes even possibility of injection of fully oxygenated water exists. For oxygenated seawater, the PREN (Pitting Resistance Equivalent Number = %Cr + 3.3 *(%Mo + 0.5 %W) + 16 %N) shall be >40 and limits are applied to the temperature4. Other applications involve Solid CRA or cladded production pipelines which may get flooded with seawater during installation and precommissioning.

Product Number: 51322-17955-SG
Author: Guru Prasad Sundararajan, Sinchana Rao, Tom Bos, Andrzej Anderko, Deepti Ballal
Publication Date: 2022
Industries: Water/Wastewater , Coatings
$0.00
$20.00
$20.00

Experimental foundation has been established for improving corrosion models for stainless steels exposed to aqueous chloride media with low levels of dissolved oxygen. Accurate repassivation potentials were measured for UNS S31603 and UNS S32305 alloys in chloride electrolytes at room and elevated temperatures using Tsujikawa-Hisamatsu Electrochemical (THE) and Cyclic Potentiodynamic Polarization (CPP) methods. It was observed that the repassivation potential values measured from CPP methods were lower than the ones obtained from THE method for the same environmental conditions. Cyclic polarization scans in aqueous chloride media were conducted at different reverse scan rates resulting in varied repassivation potentials. Medium-term corrosion potentials were measured in chloride media with controlled oxygen levels ranging from 20 – 400 ppb. These results were used as inputs for improving model prediction for repassivation and corrosion potentials. With a flexible definition of the repassivation current density, the previously developed mechanistic repassivation model reproduces the experimental repassivation potentials obtained using THE and CPP methods. Dependence of corrosion potential on dissolved oxygen has been modeled using a mixed-potential model. It has been demonstrated that the effect of agitation (caused by bubbling of oxygen) needs to be accounted for to describe the corrosion potential, especially at low dissolved oxygen where mass transport is important. 

Experimental foundation has been established for improving corrosion models for stainless steels exposed to aqueous chloride media with low levels of dissolved oxygen. Accurate repassivation potentials were measured for UNS S31603 and UNS S32305 alloys in chloride electrolytes at room and elevated temperatures using Tsujikawa-Hisamatsu Electrochemical (THE) and Cyclic Potentiodynamic Polarization (CPP) methods. It was observed that the repassivation potential values measured from CPP methods were lower than the ones obtained from THE method for the same environmental conditions. Cyclic polarization scans in aqueous chloride media were conducted at different reverse scan rates resulting in varied repassivation potentials. Medium-term corrosion potentials were measured in chloride media with controlled oxygen levels ranging from 20 – 400 ppb. These results were used as inputs for improving model prediction for repassivation and corrosion potentials. With a flexible definition of the repassivation current density, the previously developed mechanistic repassivation model reproduces the experimental repassivation potentials obtained using THE and CPP methods. Dependence of corrosion potential on dissolved oxygen has been modeled using a mixed-potential model. It has been demonstrated that the effect of agitation (caused by bubbling of oxygen) needs to be accounted for to describe the corrosion potential, especially at low dissolved oxygen where mass transport is important. 

Product tags
Also Purchased
Determination of Oxygen Limits for Corrosion Resistant Alloys (CRAs) in Oil & Gas Produced Water Based on Electrochemical Test Methods – Part 2
Available for download

Determination Of Oxygen Limits For Corrosion Resistant Alloys (Cras) In Oil & Gas Produced Water Based On Electrochemical Test Methods – Part 2.

Product Number: 51322-17947-SG
Author: Marion Duparc, Roy Johnsen, Jan Ivar Skar, Tov Eivind Saxegaard
Publication Date: 2022
$20.00

Crevice corrosion is a geometrical-dependent type of localized attack that occurs in occluded regions where a stagnant and corrosive electrolyte is in contact with the surface of a passive metal1,2. Crevices are present in all industrial designs and can lead to major failure since their detection is often challenging3,4. Main strategies for the prevention and mitigation of crevice corrosion include design awareness and adequate materials selection5.  
Picture for Evaluation of the Effect of Oxygen on CRA Materials
Available for download

51318-10799-Evaluation of the Effect of Oxygen on CRA Materials

Product Number: 51318-10799-SG
Author: Arwa Al Wahaibi / Talal Al Nabhani / Pedro Rincon Flores / Nassar Al Behalni
Publication Date: 2018
$20.00

This paper will present the testing results and the effect of oxygen on Austenitic Stainless Steel Grade 316L, Duplex Stainless Steel (22% Cr DSS) and Super Duplex Stainless Steel (25% Cr SDSS).
Picture for Materials Selection For Seawater Injection Service – Crevice Corrosion Testing Of Stainless Steels Under Controlled Dissolved Oxygen
Available for download

Materials Selection For Seawater Injection Service – Crevice Corrosion Testing Of Stainless Steels Under Controlled Dissolved Oxygen

Product Number: 51321-16527-SG
Author: K. J. Evans/ S. Chawla/ W. Huang
Publication Date: 2021
$20.00
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support