Implication Of Fractographic Analysis Of The In-Service Leak In An Above Ground Pipeline — Potential Role Of Hydrogen

Implication of Fractographic Analysis of the Crack in an Above Ground Pipeline – Potential Role of Hydrogen
Available for download

Fracture surface morphology is useful in determining the mechanisms involved in cracking. Features in the fracture surface of steel like micro-void coalescence or dimples are often related to ductile crack mode, while features like cleavage, and rock-candy showing grain boundary cracking are commonly related to brittle crack mode. Some fracture surface may have a predominant feature, while others may have presence of mixed features. Types of stress corrosion cracking (SCC) are commonly identified by the features present in the fracture surface. Features showing transgranular quasi-cleavage cracking are often related to near-neutral pH SCC, while features that show rock-candy intergranular cracking are often related to high-pH SCC [1].

Product Number: 51322-18022-SG
Author: Noelle Easter C. Co, Ming Gao, Ravi M. Krishnamurthy, Satya Kompally, Thomas Coates
Publication Date: 2022
Industry: Coatings
$0.00
$20.00
$20.00

A crack was found in 2020 on a 324 mm (12-inch) OD above ground pipeline externally uncoated but insulated with mineral wool with aluminum cladding. The steel grade of the pipeline is CSA Z245.1 Gr 414 Category II with wall thickness of 7.9 mm (0.310-inch) operating since 2013. The product that the pipeline transports is casing gas and the pipeline is operated at a temperature of 150–200 °C. The circumferential crack initiated on the outer diameter (OD) and grew through-wall. Detailed fractographic analysis showed a mixed mode of fracture: predominantly intergranular separation with a small amount of cleavage corresponding to {001} lattice plane, which is confirmed by mated fracture surfaces and the presence of {001} etching pits. Striation-like features were found on the fracture surface; however, these striation-like features are not due to fatigue. Metallographic cross section analysis also showed the crack paths are mainly intergranular with some transgranular that is consistent with micro-fractographic analysis. Classic high-pH stress corrosion cracking (SCC) mechanism cannot explain the presence of transgranular cracking, and other evidence observed such as the lack of corrosion products at the crack tip, lack of corrosion damage on the grain boundary and the lack of SCC colony on the OD surface of the pipe. These findings led to the potential role of hydrogen in the cracking mechanism observed in the above ground insulated pipeline. 

A crack was found in 2020 on a 324 mm (12-inch) OD above ground pipeline externally uncoated but insulated with mineral wool with aluminum cladding. The steel grade of the pipeline is CSA Z245.1 Gr 414 Category II with wall thickness of 7.9 mm (0.310-inch) operating since 2013. The product that the pipeline transports is casing gas and the pipeline is operated at a temperature of 150–200 °C. The circumferential crack initiated on the outer diameter (OD) and grew through-wall. Detailed fractographic analysis showed a mixed mode of fracture: predominantly intergranular separation with a small amount of cleavage corresponding to {001} lattice plane, which is confirmed by mated fracture surfaces and the presence of {001} etching pits. Striation-like features were found on the fracture surface; however, these striation-like features are not due to fatigue. Metallographic cross section analysis also showed the crack paths are mainly intergranular with some transgranular that is consistent with micro-fractographic analysis. Classic high-pH stress corrosion cracking (SCC) mechanism cannot explain the presence of transgranular cracking, and other evidence observed such as the lack of corrosion products at the crack tip, lack of corrosion damage on the grain boundary and the lack of SCC colony on the OD surface of the pipe. These findings led to the potential role of hydrogen in the cracking mechanism observed in the above ground insulated pipeline. 

Product tags
Also Purchased
Picture for Improved Girth Welding On Seamless Linepipe For High H2S Partial Pressure Condition
Available for download

Improved Girth Welding On Seamless Linepipe For High H2S Partial Pressure Condition

Product Number: 51322-17710-SG
Author: Florian Thebault, Antoine Remy, Laurent Faivre, Sébastien Leconte
Publication Date: 2022
$20.00

NACE MR0175 / ISO 15156 document part 2 provides material requirements for selecting cast irons and low-alloy steels for sour environments.1 Figure 1 is reproduced from this standard and describes different regions of environmental severity for Sulfide Stress Cracking (SSC): service in region 0 being the least susceptible to cracking, even for very sensitive materials, and region 3 being the worst.
Impact Of Material Properties Of Thick-Wall X65 TMCP Plate Steel For Sour Service
Available for download

Impact Of Material Properties Of Thick-Wall X65 TMCP Plate Steel For Sour Service

Product Number: 51322-17917-SG
Author: Thomas Haase, Christoph Bosch, Matthias Frommert, Markus Schürmann, Alexander Voelling, Sven Casper
Publication Date: 2022
$20.00

Low-alloy steel of API(1) 5L grade X65 is commonly used as line pipe material for sour service applications, where, due to stringent operation limits, resistivity to Hydrogen Induced Cracking (HIC), Sulfide Stress Cracking (SSC) and Stress-Oriented Hydrogen Induced Cracking (SOHIC) is required and tested before and after plate into pipe forming. Within recent years more challenging requirements have been introduced, including more severe corrosion test conditions, increased mechanical properties and extended limitations regarding hardness, to enable application to increasingly severe sour service conditions. For steel plants and plate manufacturers this entails the necessity to further improve the quality of their products together with separate improvements and modifications on the production plants and processes that have been implemented anyway.
Picture for Highly Durable Solventborne Silicone Organic Hybrid For Protective Coating Applications
Available for download

Highly Durable Solventborne Silicone Organic Hybrid For Protective Coating Applications

Product Number: 51322-17537-SG
Author: Dr. Erin Vogel, Dr. Gary Wieber,Dr. Adam Tomasik, Dr. Yanxiang Li,
Publication Date: 2022
$20.00

The impact of corrosion on society is enormous. The National Association of Corrosion Engineers (NACE) estimated that the global total cost of corrosion is ~$2.5 trillion (USD), approximately 3.4% of global GDP.1 In 2016, NACE released the “International Measures of Prevention, Applications, and Economics of Corrosion Technology” which estimates that implementing corrosion prevention best General Business practices could result in global savings between 13-15 percent of the cost of damage, or a savings between $375-875 billion (USD) annually on a global basis.
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support