51318-10736-Effect of various alkanolamines on the corrosion behavior of N80 steel in impure SC-CO2 environments

Picture for Effect of various alkanolamines on the corrosion behavior of N80 steel in impure SC-CO2 environments
Available for download

The effect of monoethanolamine (MEA), diethanolamine (DEA) and N-methyldiethanolamine (MDEA) on the corrosion behavior of N80 steel in water-saturated supercritical CO2 phase and supercritical CO2-saturated aqueous phase with impurities (SO2, NO2 and O2).

Product Number: 51318-10736-SG
Author: Yong Xiang / Chen Li / Zhengwei Long / Wei Yan
Publication Date: 2018
Industry: Science of Corrosion
$0.00
$20.00
$20.00

The use of alkanolamines is regarded as the most commonly used way in carbon capture and storage system (CCS) for carbon dioxide capture due to their best comprehensive effect compared with other methods. This work investigated the effect of monoethanolamine (MEA), diethanolamine (DEA) and N-methyldiethanolamine (MDEA) on the corrosion behavior of N80 steel in water-saturated supercritical

CO2 phase and supercritical CO2-saturated aqueous phase with impurities (SO2, NO2 and O2). The

results by weight-loss measurements showed that all the tested alkanolamines inhibited corrosion, and the inhibition efficiency of the three alkanolamines at a concentration of 300 ppmv was between 55% and 67% in the aqueous phase, whereas the inhibition efficiencies were low in the water-saturated supercritical CO2 phase. The off-line pH measurements indicated that alkanolamines could increase the pH value of the solution. Scanning electron microscopy (SEM) was employed to investigate the surface morphology of the corroded specimens after corrosion for 24 h, and 3-dimensional profilometer was applied to measure the pitting rate of specimens after the removal of corrosion products. Chemical and phase compositions of corrosion products were tested by energy dispersive X-ray spectroscopy (EDS) and X-ray diffraction (XRD), respectively.

Key words: CCS, alkanolamine, supercritical CO2, impurity, inhibition efficiency

The use of alkanolamines is regarded as the most commonly used way in carbon capture and storage system (CCS) for carbon dioxide capture due to their best comprehensive effect compared with other methods. This work investigated the effect of monoethanolamine (MEA), diethanolamine (DEA) and N-methyldiethanolamine (MDEA) on the corrosion behavior of N80 steel in water-saturated supercritical

CO2 phase and supercritical CO2-saturated aqueous phase with impurities (SO2, NO2 and O2). The

results by weight-loss measurements showed that all the tested alkanolamines inhibited corrosion, and the inhibition efficiency of the three alkanolamines at a concentration of 300 ppmv was between 55% and 67% in the aqueous phase, whereas the inhibition efficiencies were low in the water-saturated supercritical CO2 phase. The off-line pH measurements indicated that alkanolamines could increase the pH value of the solution. Scanning electron microscopy (SEM) was employed to investigate the surface morphology of the corroded specimens after corrosion for 24 h, and 3-dimensional profilometer was applied to measure the pitting rate of specimens after the removal of corrosion products. Chemical and phase compositions of corrosion products were tested by energy dispersive X-ray spectroscopy (EDS) and X-ray diffraction (XRD), respectively.

Key words: CCS, alkanolamine, supercritical CO2, impurity, inhibition efficiency

Product tags
Also Purchased
Picture for Polyaniline/Silicon Dioxide Containing Coating for Use in Artificial Geothermal Brines
Available for download

51318-10708-Polyaniline/Silicon Dioxide Containing Coating for Use in Artificial Geothermal Brines

Product Number: 51318-10708-SG
Author: Gabriela Aristia / Christina Roth / Ralph Bäßler
Publication Date: 2018
$20.00

An artificial geothermal water was used to investigate the performance of high alloyed materials. The electrolyte has pH 4 and contains 1,500 mg/l Cl-, 20 mg/l SO42-, 15 mg/l HCO3-, 200 mg/l Ca2+, 250 mg/l K+, and 600 mg/l Na+.
Picture for 51318-10798-Development of a Practical Model for H2S Corrosion Prediction for Upstream Oil and Gas Applications
Available for download

51318-10798-Development of a Practical Model for H2S Corrosion Prediction for Upstream Oil and Gas Applications

Product Number: 51318-10798-SG
Author: J. Sonke / Y. Zheng / W.M. Bos
Publication Date: 2018
$20.00

An improved sour corrosion model was developed based on: • A bare steel sour electrochemical corrosion model, derived from published literature • Mechanisms that affect scale performance and trigger localised corrosion • A specific elemental sulphur degradation mechanism • Corrosion mitigation strategy

 
Picture for Environmentally Assisted Cracking of High Strength Nickel Based Alloys Under Cathodic Protection
Available for download

51318-10700-Environmentally Assisted Cracking of High Strength Nickel Based Alloys Under Cathodic Protection

Product Number: 51318-10700-SG
Author: Ramopal Thodla
Publication Date: 2018
$20.00

Environmentally assisted cracking of high strength nickle based alloys was investigated in 3.5wt% NaCl under cathodic protection.
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support