Corrosion, either internal or external, along with other types of defects on pipelines eventually lead to leaks without proper treatment. This gives rise to several issues, including environmental and safety hazards, and in case of pipe leaks in a plant, a loss of the efficiency of the process or, ultimately, failure of the process. Replacing the corroded pipelines (piping) can be difficult, costly and time consuming especially for plant. A required shutdown causes major economic loss. Thus, instead of a replacement of the defected pipelines, the installation of online repair is a better option.
Repairs of pipelines include metallic and non-metallic repairs. Metallic repairs generally require welding or hot works which is not suitable for online repair of pipes containing hydrocarbons. In such cases the use of non-metallic composite repairs is the optimum solution. A non-metallic composite repair system is a system used to reinforce structures using a fiber equipped with a thermoset epoxy system. The epoxy system consists of a hardener and a resin which, after mixing, become solid through a polymerization reaction after a short duration of time, a process that is called curing. Depending on the temperature, the duration of time changes in an inverse relation. The higher the temperature, the smaller the duration of time needed for curing. This system can be used to reinforce pipelines with both external and internal corrosion and it can be used on Straight Pipes, Tees, Elbows, Flanges and weld joints. The repair system can also be installed online without the need for a shutdown in a short amount of time and a small requirement of labor intensity, making it cost effective. It is also environmentally friendly. In this paper we are going to present cases that were resolved by our company that demonstrate how successful these non-metallic composite repairs are and how diverse their applications can be

Materials properties that are used in specific oil and gas environments are de-rated due to the risks associated with hydrogen embrittlement cracking. In oil production environments the concern is for the onset of stress corrosion cracking (SCC), while in seawater environments the concern is for Hydrogen Induced Stress Cracking (HISC). Both are hydrogen embrittlement phenomena with the distinction being the source of hydrogen for each. In SSC the source of hydrogen is from the presence of H2S in the oil production fluids, and in HISC the source of hydrogen is from the dissociation of water from the cathodic protection system. This paper is focused on the latter phenomena and aims to characterize the susceptibility of carbon alloy steels as applied in fastener applications, in a seawater environment under cathodic protection.