97024 STUDY OF X80 GRADE HIGH STRENGTH LINE PIPE FOR SOUR SERVICE

Picture for 97024 STUDY OF X80 GRADE HIGH STRENGTH
Available for download
Product Number: 51300-97024-SG
ISBN: 97024 1997 CP
Author: J. Fujino, A. Yamamoto, K.Ohnishi, T. Kushida, S. Okaguchi, M. Hamada
$0.00
$20.00
$20.00
X80 grade high strength large diameter line pipe (UOE Pipe) for sour service has been studied. Increasing Mn content to provide strength of X80 increases HIC susceptibility due to center segregation of Mn in continuously cast slabs. The Mn content should be controlled less than 1.4% to maintain HIC resistance in the NACE TM0177 solution. The required strength can be obtained by addition of 0.5% Cr and accelerated controlled cooling after rolling. It has been clarified that Cr is very useful in providing high strength over X70 without accelerating the center segregation of Mn. SSC resistance can be improved by controlling maximum hardness of weld metal lower than 230Hv. Sour service X80 UOE pipes of two sizes were manufactured on large scales based on these experimental results. These pipes showed good low temperature toughness and HIC resistance in the NACE TM0177 solution. Keywords: HIC, SSC, X80, large diameter line pipe, segregation, low Cr, accelerated controlled cooling, Weld
X80 grade high strength large diameter line pipe (UOE Pipe) for sour service has been studied. Increasing Mn content to provide strength of X80 increases HIC susceptibility due to center segregation of Mn in continuously cast slabs. The Mn content should be controlled less than 1.4% to maintain HIC resistance in the NACE TM0177 solution. The required strength can be obtained by addition of 0.5% Cr and accelerated controlled cooling after rolling. It has been clarified that Cr is very useful in providing high strength over X70 without accelerating the center segregation of Mn. SSC resistance can be improved by controlling maximum hardness of weld metal lower than 230Hv. Sour service X80 UOE pipes of two sizes were manufactured on large scales based on these experimental results. These pipes showed good low temperature toughness and HIC resistance in the NACE TM0177 solution. Keywords: HIC, SSC, X80, large diameter line pipe, segregation, low Cr, accelerated controlled cooling, Weld
PRICE BREAKS - The more you buy, the more you save
Quantity
1+
5+
Price
$20.00
$20.00
Product tags
Also Purchased
Picture for 99428 Sulfide Stress Cracking of a Pipeline
Available for download

99428 Sulfide Stress Cracking of a Pipeline Weld in Sour Gas Service

Product Number: 51300-99428-SG
ISBN: 99428 1999 CP
Author: K. E. Szklarz
$20.00
Picture for Development of Sour Service Offshore High Strength and Heavy Wall Line Pipe DSAW Process
Available for download

51313-02580-Development of Sour Service Offshore High Strength and Heavy Wall Line Pipe DSAW Process

Product Number: 51313-02580-SG
ISBN: 02580 2013 CP
Author: Tribhuwan Kathayat
Publication Date: 2013
$20.00
Picture for 97058 RIPPLED STRAIN RATE TEST FOR CRA
Available for download

97058 RIPPLED STRAIN RATE TEST FOR CRA SOUR SERVICE MATERIALS SELECTION

Product Number: 51300-97058-SG
ISBN: 97058 1997 CP
Author: W.J.R.Nisbet, R.H.C. Hartman, G. van den Handel
$20.00
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support