The Influence of Flow Rate on Corrosion Behavior of X65 Carbon Steel in Water-Saturated Supercritical CO2/H2S System

The influence of flow rate on corrosion behavior of X65 carbon steel in water-saturated supercritical CO2 phase containing 1000 ppmv H2S impurity was studied at 35 °C and 8 MPa from 0 m/s to 1.5 m/s. Weight loss tests showed that the general corrosion rate reached maximum at the flow rate of 1 m/s and then decreased with flow rate to 1.5 m/s. Turtle pattern corrosion morphology was observed on the sample surface when the flow rate exceeded 1 m/s. The corrosion product mainly consisted of FeCO3 and FeS and the average size of spherical corrosion product changed with flow rate. Besides the percentage composition of FeS presented the same change trend as the average size of spherical corrosion product. In supercritical CO2 phase wall shear stress was not big enough to cause mechanical damage on corrosion film but can affect the formation process and the characteristics of the corrosion film of X65 carbon steel.

Product Number: 51319-13081-SG
Author: Jian Bo Sun
Publication Date: 2019
$0.00
$20.00
$20.00
Also Purchased
Picture for 08470 Top of the Line Corrosion in H2S/CO2 Environment
Available for download

08470 Top of the Line Corrosion in H2S/CO2 Environment

Product Number: 51300-08470-SG
ISBN: 08470 2008 CP
Author: Alvaro Camacho, Marc Singer, Bruce N. Brown, and Srdjan Nesic
Publication Date: 2008
$20.00
Picture for Comparison of corrosion behavior of X65 pipeline steel in CO2-H2S and CO2 environment at different f
Available for download

51312-01238-Comparison of corrosion behavior of X65 pipeline steel in CO2-H2S and CO2 environment at different f

Product Number: 51312-01238-SG
ISBN: 01238 2012 CP
Author: Wei Liu
Publication Date: 2012
$20.00