51314-3835-Sulfide Stress Corrosion Cracking of a Spiral Weld Pipeline in Sour Service

Picture for Sulfide Stress Corrosion Cracking of a Spiral Weld Pipeline in Sour Service
Available for download
Product Number: 51314-3835-SG
ISBN: 3835 2014 CP
Author: Abdul Razzaq Al-Shamari
Publication Date: 2014
$0.00
$0.00
$0.00
Some pipelines used to transport high pressure gas to long distances are made from carbon steel plates by spiral welding. There are instances in which such pipelines gave a long service in sour atmospheres. But when they failed they failed catastrophically and sometimes repeated failures occurred.In one such instance the pipeline in the subject case gave a service life of about 12 years in sour gas service. In year 2012 the pipeline failed suddenly by cracking along the heat affected zone of the spiral weld. Onwards frequent failures began to occur in identical fashion at different locations. This prompted for a failure investigation to be carried out. Mechanical metallurgical and chemical tests and analyses have been carried out to understand the natures of the failures.The paper presents the findings and a discussion on the correlation of mechanical metallurgical and chemistry parameters to the type of failure that has occurred.Keywords: Spiral weld pipelines sour gas cracking. 
Some pipelines used to transport high pressure gas to long distances are made from carbon steel plates by spiral welding. There are instances in which such pipelines gave a long service in sour atmospheres. But when they failed they failed catastrophically and sometimes repeated failures occurred.In one such instance the pipeline in the subject case gave a service life of about 12 years in sour gas service. In year 2012 the pipeline failed suddenly by cracking along the heat affected zone of the spiral weld. Onwards frequent failures began to occur in identical fashion at different locations. This prompted for a failure investigation to be carried out. Mechanical metallurgical and chemical tests and analyses have been carried out to understand the natures of the failures.The paper presents the findings and a discussion on the correlation of mechanical metallurgical and chemistry parameters to the type of failure that has occurred.Keywords: Spiral weld pipelines sour gas cracking. 
Product tags
Also Purchased
Picture for 99428 Sulfide Stress Cracking of a Pipeline
Available for download

99428 Sulfide Stress Cracking of a Pipeline Weld in Sour Gas Service

Product Number: 51300-99428-SG
ISBN: 99428 1999 CP
Author: K. E. Szklarz
$20.00
Picture for Pipeline Integrity Management Through Internal Corrosion Monitoring
Available for download

51314-3834-Pipeline Integrity Management Through Internal Corrosion Monitoring

Product Number: 51314-3834-SG
ISBN: 3834 2014 CP
Author: Abdul Razzaq Al-Shamari
Publication Date: 2014
$0.00
Picture for 00157 LIMITS OF LINEPIPE WELD HARDNESS FOR
Available for download

00157 LIMITS OF LINEPIPE WELD HARDNESS FOR DOMAINS OF SOUR SERVICE IN OIL AND GAS PRODUCTION

Product Number: 51300-00157-SG
ISBN: 00157 2000 CP
Author: M B Kermani, C Boucher, J L Crolet, J Enerhaug, P Fassina, R Howard, J p Jansen, C Linne, R Popperli
$20.00
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support