51316-7323-Study of protection mechanism of multifunctional coating systems against internal corrosion in pipelines in oil and gas industry

Picture for Study of protection mechanism of multifunctional coating systems against internal corrosion in pipel
Available for download

Organic coating systems for protection against internal corrosion of pipelines are important to maintain integrity of oil and gas infrastructure. The present investigation focuses on evaluation of protective properties of a set of multiphase coating systems in the environment encountered inside of off-shore natural gas pipelines.

Product Number: 51316-7323-SG
ISBN: 7323 2016 CP
Author: Nasser AlJassem
Publication Date: 2016
Industries: Gas/Liquid Pipelines , Coatings and Linings
$0.00
$20.00
$20.00

 The organic coating systems for protection against internal corrosion of pipelines have recently received considerable attention due to their importance in maintaining the integrity of oil and gas infrastructure. Natural gas pipelines in Qatar are subject to both corrosion and erosion due to the detrimental actions of seawater and sand. The present investigation focuses on evaluation of protective properties of a set of multiphase coating systems in the environment encountered inside of off-shore natural gas pipelines. These coatings are multifunctional coatings systems that promise to provide simultaneous corrosion protection and wear resistance. The coatings ranged in thickness and amount of abrasion-resistant ceramic filler. The sweet oil and natural gas environment in Qatar was simulated by a carbon dioxide (CO2) saturated solutions with 2000 ppm Cl- ions at pH 4, at 60oC and atmospheric pressure. Two types of defects were intentionally introduced into the coatings by tribology tester and their response to corrosion environment was studied. The surface topography before and after defects introduction was evaluated by 3-D profilometry. A stereoscope was employed to characterize the morphology of studied coatings. The electrochemical performances and degradations of coated steel panels in tested solution were characterized by electrochemical impedance spectroscopy (EIS) and open circuit potential (OCP) measurements. Different formulations of the organic coating systems had shown a significant change in the impedance response, with immersion time. The data from EIS measurements were fitted into equivalent circuits and the values of their components were calculated and used to understand the interactions between the coating systems and the solution interfaces.

Key Words: downloadable,  EIS, profilometer, organic coating, corrosion, wear.

 

 The organic coating systems for protection against internal corrosion of pipelines have recently received considerable attention due to their importance in maintaining the integrity of oil and gas infrastructure. Natural gas pipelines in Qatar are subject to both corrosion and erosion due to the detrimental actions of seawater and sand. The present investigation focuses on evaluation of protective properties of a set of multiphase coating systems in the environment encountered inside of off-shore natural gas pipelines. These coatings are multifunctional coatings systems that promise to provide simultaneous corrosion protection and wear resistance. The coatings ranged in thickness and amount of abrasion-resistant ceramic filler. The sweet oil and natural gas environment in Qatar was simulated by a carbon dioxide (CO2) saturated solutions with 2000 ppm Cl- ions at pH 4, at 60oC and atmospheric pressure. Two types of defects were intentionally introduced into the coatings by tribology tester and their response to corrosion environment was studied. The surface topography before and after defects introduction was evaluated by 3-D profilometry. A stereoscope was employed to characterize the morphology of studied coatings. The electrochemical performances and degradations of coated steel panels in tested solution were characterized by electrochemical impedance spectroscopy (EIS) and open circuit potential (OCP) measurements. Different formulations of the organic coating systems had shown a significant change in the impedance response, with immersion time. The data from EIS measurements were fitted into equivalent circuits and the values of their components were calculated and used to understand the interactions between the coating systems and the solution interfaces.

Key Words: downloadable,  EIS, profilometer, organic coating, corrosion, wear.

 

Product tags
Also Purchased
Picture for 10002 Failure Analysis of Three Layer Polypropylene Pipeline Coatings
Available for download

10002 Failure Analysis of Three Layer Polypropylene Pipeline Coatings

Product Number: 51300-10002-SG
ISBN: 10002 2010 CP
Author: Ali Noor Moosavi, Benjamin T. A. Chang and Kamal Mohamed Morsi
Publication Date: 2010
$20.00

Three layer polypropylene (3LPP) pipeline coatings failed prematurely in the oilfields of Abu Dhabi in the United Arab Emirates (UAE). A failure investigation and analysis into this phenomenon was instigated. The coating disbondment has been found to be due to high residual stress concentration and adhesion loss.
Picture for 11032 New Development of a High Tg FBE Coating
Available for download

11032 New Development of a High Tg FBE Coating

Product Number: 51300-11032-SG
ISBN: 2011 11032 CP
Author: Byungsoo Moon, Byungkap Paek, Jinseok Lee, Hyunwoong Wang, Namho Lee
Publication Date: 2011
$20.00

Fusion Bonded Epoxy (FBE) is required to protect the pipes in higher temperatures. This paper reports evaluation methods for these high Tg FBE, and the performance differences between the high Tg FBE and general FBE.
Picture for Pipeline Corrosion Management; a Compendium
Available for download

51314-3723-Pipeline Corrosion Management; a Compendium

Product Number: 51314-3723-SG
ISBN: 3723 2014 CP
Author: Bijan Kermani
Publication Date: 2014
$0.00

This paper summarizes major elements of a recent recommended practice (RP) on Pipeline Corrosion Management (PCM) published by the European Federation of Corrosion (EFC). The RP goes into details on a methodical approach to carrying out PCM.
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support