Sour Service Limit Of 17% Cr Stainless Steels Grades For OCTG

Product Number: 51321-16637-SG
Author: Toshiyuki SUNABA/ Susumu HIRANO/ Thiago MESQUITA/ FranceHerve MARCHEBOIS/ Thierry CASSAGNE
Publication Date: 2021
$0.00
$20.00
$20.00

Recently, the use of 17% Cr seamless steel tubing has been a cost-effective solution for preventing high pressure and high temperature (HP/HT) CO2 corrosion environment with small amount of H2S. This paper focuses on the sulfide stress cracking (SSC) results of 17% Cr stainless steels in simulated conditions for HP/HT gas wells. In the frame of a qualification program, NACEa Standard Tensile Test, Method A was adopted in accordance with NACE TM0177. The influence of partial pressure of H2S was investigated at condensed and formation water conditions where SSC is likely to occur. In addition, a previous work on the localized corrosion and the stress corrosion cracking behavior of those grade is also discussed in this paper. The results were summarized in a sour service domain map and compared with previous published data. The results showed the applicability of this alloy for selected gas well conditions. .

Key words: 17%Cr, OCTG, CO2, H2S, SSC

Recently, the use of 17% Cr seamless steel tubing has been a cost-effective solution for preventing high pressure and high temperature (HP/HT) CO2 corrosion environment with small amount of H2S. This paper focuses on the sulfide stress cracking (SSC) results of 17% Cr stainless steels in simulated conditions for HP/HT gas wells. In the frame of a qualification program, NACEa Standard Tensile Test, Method A was adopted in accordance with NACE TM0177. The influence of partial pressure of H2S was investigated at condensed and formation water conditions where SSC is likely to occur. In addition, a previous work on the localized corrosion and the stress corrosion cracking behavior of those grade is also discussed in this paper. The results were summarized in a sour service domain map and compared with previous published data. The results showed the applicability of this alloy for selected gas well conditions. .

Key words: 17%Cr, OCTG, CO2, H2S, SSC

Product tags
Also Purchased
Picture for Enhanced Corrosion-Resistant Stainless Steel OCTG of 17Cr for Sweet and Sour Environments
Available for download

51313-02436-Enhanced Corrosion-Resistant Stainless Steel OCTG of 17Cr for Sweet and Sour Environments

Product Number: 51313-02436-SG
ISBN: 02436 2013 CP
Author: Yasuhide Ishiguro
Publication Date: 2013
$20.00