Sensitization Resistance of Alloy UNS N08825 After Different Mill-Annealing Temperatures and Times

Product Number: 51321-16395-SG
Author: Julia Botinha/Bodo Gehrmann/Peter Maas/Helena Alves
Publication Date: 2021
$0.00
$20.00
$20.00

Designed for applications in the chemical process industry and later also used in the Oil & Gas industry, Alloy UNS(1) N08825 is a fully austenitic nickel-iron-chromium alloy, stabilized by titanium and with additions of copper and molybdenum. It is well known that the susceptibility of the material to intergranular corrosion in the “as delivered” (mill-annealed) condition, so as after the exposure of the material to intermediate temperatures, is strongly dependent on the chemical composition and additionally on the thermal history. This work consists on the variation of the nickel content within the UNS chemical composition of Alloy N08825 and the variation of the annealing temperatures and times in order to better understand the influence of these variables on the intergranular corrosion resistance of material from large-scale production. Samples were tested according to ASTM(2) G28 method A in the “as delivered” condition and after sensitization heat treatment to verify its intergranular corrosion resistance.

Key words: UNS N08825, Alloy 825, Intergranular corrosion resistance, heat treatment, annealing temperature, ASTM G28 A, sensitization behavior

Designed for applications in the chemical process industry and later also used in the Oil & Gas industry, Alloy UNS(1) N08825 is a fully austenitic nickel-iron-chromium alloy, stabilized by titanium and with additions of copper and molybdenum. It is well known that the susceptibility of the material to intergranular corrosion in the “as delivered” (mill-annealed) condition, so as after the exposure of the material to intermediate temperatures, is strongly dependent on the chemical composition and additionally on the thermal history. This work consists on the variation of the nickel content within the UNS chemical composition of Alloy N08825 and the variation of the annealing temperatures and times in order to better understand the influence of these variables on the intergranular corrosion resistance of material from large-scale production. Samples were tested according to ASTM(2) G28 method A in the “as delivered” condition and after sensitization heat treatment to verify its intergranular corrosion resistance.

Key words: UNS N08825, Alloy 825, Intergranular corrosion resistance, heat treatment, annealing temperature, ASTM G28 A, sensitization behavior

Also Purchased
Picture for The Sensitisation Behaviour of Alloy UNS N08825 After Heat Treatment as Used in Clad Materials
Available for download

The Sensitisation Behaviour of Alloy UNS N08825 After Heat Treatment as Used in Clad Materials

Product Number: 51317--9459-SG
ISBN: 9459 2017 CP
Author: Helena Alves
Publication Date: 2017
$20.00

The aim of this paper is to present recent standard test corrosion data obtained in laboratory for alloy UNS N08825 after post weld heat treatment in comparison with as delivered (soft annealed) material.

 

Picture for 11361 Processing and Fabricating Alloy 825 for Optimized Properties and Corrosion Resistance
Available for download

11361 Processing and Fabricating Alloy 825 for Optimized Properties and Corrosion Resistance

Product Number: 51300-11361-SG
ISBN: 2011 11361 CP
Author: Lewis Shoemaker and Jim Crum
Publication Date: 2011
$20.00
Picture for 97520 PRECIPITATION REACTIONS AND CORROSION
Available for download

97520 PRECIPITATION REACTIONS AND CORROSION RESISTANCE OF THERMALLY AGED AND WELDED ALLOY 825

Product Number: 51300-97520-SG
ISBN: 97520 1997 CP
Author: T. Nagashima, J. R. Crum, C. S. Tassen
$20.00