Role of Material Condition on Precursor Corrosion Damage and Stress Corrosion Crack Initiation Behavior of Alloy 600 in PWR Primary Water

Stress corrosion crack (SCC) initiation testing has been performed on a 15% cold-worked UNS N06600 (Alloy 600) heat in mill-annealed (MA), solution annealed (SA), and thermally treated (TT) conditions to assess the role of grain boundary (GB) carbides on stress-assisted intergranular attack (IGA) and short crack nucleation and growth. The SCC initiation tests were conducted at a constant load equivalent to the materials’ yield stress in 360oC simulated pressurized water reactor primary water. Results revealed the highest SCC initiation susceptibility occurred in the Alloy 600 MA material, followed by the TT and SA materials, suggesting that GB carbide distribution did not have a controlling effect on SCC initiation resistance. Quantitative assessments of IGA and short cracks were conducted to help understand this phenomenon, and the role of GB carbides in precursor damage development that leads to differences in macroscopic SCC initiation behavior are discussed. 

Product Number: 51320-14536-SG
Author: Ziqing Zhai, Mychailo Toloczko, Stephen Bruemmer
Publication Date: 2020
$0.00
$20.00
$20.00
Also Purchased
Picture for 03538 THE EFFECT OF STRAIN RATE ON PWSCC
Available for download

03538 THE EFFECT OF STRAIN RATE ON PWSCC FRACTURE MODE OF ALLOY 600(UNS N06600) AND 304 STAINLESS STEEL(UNS S30400)

Product Number: 51300-03538-SG
ISBN: 03538 2003 CP
Author: Nobuo Totsuka, Yoshito Nishikawa, Yoshiari Kaneshima, Koji Arioka
$20.00
Picture for 00221 SCC CRACK GROWTH RATES OF TYPE 304
Available for download

00221 SCC CRACK GROWTH RATES OF TYPE 304 STAINLESS STEEL AT HIGH K REGION IN SIMULATED BWR ENVIRONMENT

Product Number: 51300-00221-SG
ISBN: 00221 2000 CP
Author: M. Itow and M. Kikuchi, S. Suzuki
$20.00