51315-6199-Hydrogen Cracking of Legacy Steels

Picture for Hydrogen Cracking of Legacy Steels
Available for download
Product Number: 51315-6199-SG
ISBN: 6199 2015 CP
Author: Frank Dean
Publication Date: 2015
$0.00
$20.00
$20.00
Steel in sour corrosive service is prone to various forms of hydrogen induced cracking (HIC). This can take several forms such as centre line cracking surface blisters and stress oriented HIC (SOHIC).In this paper we consider the effect of the corrosion scenario steel microstructural heterogeneity steel surface condition and scales on the type of damage that is manifest particularly in reference to legacy steels which are more prone to HIC. It is hoped the paper will contribute to our knowledge of both the cause of HIC damage manifest in damaged pipe and the susceptibility to HIC that can be expected from legacy steels which face prospectively more severe sour service.
Steel in sour corrosive service is prone to various forms of hydrogen induced cracking (HIC). This can take several forms such as centre line cracking surface blisters and stress oriented HIC (SOHIC).In this paper we consider the effect of the corrosion scenario steel microstructural heterogeneity steel surface condition and scales on the type of damage that is manifest particularly in reference to legacy steels which are more prone to HIC. It is hoped the paper will contribute to our knowledge of both the cause of HIC damage manifest in damaged pipe and the susceptibility to HIC that can be expected from legacy steels which face prospectively more severe sour service.
Also Purchased
Picture for Hydrogen in Steels: A Critical Review and Recommended Practices
Available for download

Hydrogen in Steels: A Critical Review and Recommended Practices

Product Number: 51317--9548-SG
ISBN: 9548 2017 CP
Author: Mark Sadowski
Publication Date: 2017
$20.00

A summary of hydrogen bakeout history to remove hydrogen from a component. Existing recommendations regarding hydrogen bakeout in codes and standards. Results from an industry survey of energy producers. Proposed methodology for selecting bakeout parameters.

 

 
Picture for Hydrogen Induced Cracking Safe Materials Operating Limits
Available for download

51315-5498-Hydrogen Induced Cracking Safe Materials Operating Limits

Product Number: 51315-5498-SG
ISBN: 5498 2015 CP
Author: Roberto Morana
Publication Date: 2015
$20.00
Picture for 09120 - Hydrogen Effects on High Strength Pipeline Steels
Available for download

09120 Hydrogen Effects on High Strength Pipeline Steels

Product Number: 51300-09120-SG
ISBN: 09120 2009 CP
Author: Jeffrey Xie, Fraser King, Robert Yang
Publication Date: 2009
$20.00
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support