Evaluation Of Titanium 475 Alloy For Use In Oil And Gas Environments

Picture for Evaluation Of Titanium 475 Alloy For Use In Oil And Gas Environments
Available for download

ASTM Grade 29 titanium alloy (UNS R56404) has been traditionally used for oil and gas stress joints (TSJ). However, given the general difficulty of processing this type of alloy in the beta quenched condition and more recently the exorbitant increase in alloying costs due to the ruthenium, a new solution is required if titanium is to be considered for future applications. This 475 alloy was developed to meet geothermal requirements to replace Grade 29 seamless casing. The essential material properties of Grade 29 in bulk and welded condition as used for titanium stress joints were reported by Shutz et al.

Product Number: 51322-17840-SG
Author: William. D. MacDonald, Mikel Hogan, Dennis Dunlap
Publication Date: 2022
Industries: Corrosion Monitoring and Control , Coatings and Linings , Coatings
$0.00
$20.00
$20.00

A new titanium alloy, TIMETAL® 475 (Ti-475), which was developed for use in aggressive geothermal fields as a casing material, has been tested for use in typical oil and gas environments. The alloy composition, Ti-0.4Ni-3.75Mo-0.75Zr, provides excellent corrosion resistance in geothermal brines which are low pH and high in chlorides. For oil and gas applications, the additional effects of H2S and CO2 on the alloy must be considered. To this end, the alloy was subjected to the NACE TM-0177 Level VII exposure test. For the geothermal application, the alloy is prepared in the Solution Treated and Aged (STA) condition with a typical titanium bimodal microstructure. For use in oil and gas, the alloy is prepared in the Beta Annealed condition. The beta annealed condition is required for large components such as titanium stress joints where superior fatigue properties are required. This paper reviews the mechanical properties and corrosion evaluation of the Ti-475 alloy in the beta annealed condition as compared to the STA condition.

A new titanium alloy, TIMETAL® 475 (Ti-475), which was developed for use in aggressive geothermal fields as a casing material, has been tested for use in typical oil and gas environments. The alloy composition, Ti-0.4Ni-3.75Mo-0.75Zr, provides excellent corrosion resistance in geothermal brines which are low pH and high in chlorides. For oil and gas applications, the additional effects of H2S and CO2 on the alloy must be considered. To this end, the alloy was subjected to the NACE TM-0177 Level VII exposure test. For the geothermal application, the alloy is prepared in the Solution Treated and Aged (STA) condition with a typical titanium bimodal microstructure. For use in oil and gas, the alloy is prepared in the Beta Annealed condition. The beta annealed condition is required for large components such as titanium stress joints where superior fatigue properties are required. This paper reviews the mechanical properties and corrosion evaluation of the Ti-475 alloy in the beta annealed condition as compared to the STA condition.

Product tags
Also Purchased
Picture for Failure Analysis Of Hydrotested 12-Inch Type 304 SS Pipe Sections
Available for download

Failure Analysis Of Hydrotested 12-Inch Type 304 SS Pipe Sections

Product Number: 51322-17852-SG
Author: Sudhakar Mahajanam, Chris Miller, Cody Robinson, Scott Harding, Amilcar Oberto
Publication Date: 2022
$20.00

Pre-commissioning hydrostatic testing of pipelines and the resulting corrosion (MIC) issues are often linked to test water quality, as well as post-test cleaning operations. In a 1998 study, it was reported that localized corrosion (pitting/crevice corrosion) accounted for 20% of failures in the chemical process industry with an estimated one half of those being MIC failures. Identification of MIC failures is not straightforward. Common characteristic features such as pit clustering, “tunneling” of pits, tuberculation, high microbiological counts, presence of sulfides (in the case of sulfate reducing bacteria (SRB)) and preferential weld attack have been used to anecdotally pinpoint field failures towards MIC.
Picture for 08084 A New High Strength Corrosion Resistant Alloy for Oil and Gas Applications
Available for download

08084 A New High Strength Corrosion Resistant Alloy for Oil and Gas Applications

Product Number: 51300-08084-SG
ISBN: 08084 2008 CP
Author: Sarwan K. Mannan and Shaelesh Patel
Publication Date: 2008
$20.00
Picture for 10336 A New Corrosion-Resistant NI-MO-CR Alloy for the Most Versatile Environments
Available for download

10336 A New Corrosion-Resistant NI-MO-CR Alloy for the Most Versatile Environments

Product Number: 51300-10336-SG
ISBN: 10336 2010 CP
Author: Nacéra Sabrina Meck, P. Crook and P. E. Manning
Publication Date: 2010
$20.00
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support