51313-02589-Evaluation of the Seabed Temperature SSC Resistance of Weldable Martensitic 13% Chromium SS

Picture for Evaluation of the Seabed Temperature SSC Resistance of Weldable Martensitic 13% Chromium SS
Available for download
Product Number: 51313-02589-SG
ISBN: 02589 2013 CP
Author: Philip Dent
Publication Date: 2013
$0.00
$20.00
$20.00

Weldable Martensitic 13% Chromium Stainless Steels (WMSS) are used for mildly sour welded flow-lines in the oil and gas industry as an alternative to inhibited carbon steel or lined pipe.

For most material selection and qualification programmes for sour applications the material is tested in accordance with NACE MR0175 / ISO 15156 at the maximum design temperature and at ambient temperature (i.e. 24 ±3°C). However WMSS may be more susceptible to sulphide stress cracking (SSC) below ambient temperature and current information in the literature is limited. Consequently qualification to the requirements of NACE MR0175 / ISO 15156 may show acceptable results whereas in-service cracking could result due to exposure to temperatures below ambient. This may not be applicable for some applications however for sub-sea pipelines the typical seabed temperature is in the region of 4°C which may be experienced during ‘shut-in’ conditions.

SSC testing has been undertaken on WMSS at ambient and seabed temperatures using four point bend (FPB) specimens in simulated condensed water (CW) and produced water (PW) environments at two partial pressures of H2S for parent line-pipe in the as-received and machined conditions. In addition a test method has been developed to closely control the test parameters with particular regard to dissolved oxygen and pH in order to ensure consistency of results. The test results will be presented and the SSC performance of the material will be discussed with consideration to the test temperature pH partial pressure of H2S and surface condition of the specimens.
 

Weldable Martensitic 13% Chromium Stainless Steels (WMSS) are used for mildly sour welded flow-lines in the oil and gas industry as an alternative to inhibited carbon steel or lined pipe.

For most material selection and qualification programmes for sour applications the material is tested in accordance with NACE MR0175 / ISO 15156 at the maximum design temperature and at ambient temperature (i.e. 24 ±3°C). However WMSS may be more susceptible to sulphide stress cracking (SSC) below ambient temperature and current information in the literature is limited. Consequently qualification to the requirements of NACE MR0175 / ISO 15156 may show acceptable results whereas in-service cracking could result due to exposure to temperatures below ambient. This may not be applicable for some applications however for sub-sea pipelines the typical seabed temperature is in the region of 4°C which may be experienced during ‘shut-in’ conditions.

SSC testing has been undertaken on WMSS at ambient and seabed temperatures using four point bend (FPB) specimens in simulated condensed water (CW) and produced water (PW) environments at two partial pressures of H2S for parent line-pipe in the as-received and machined conditions. In addition a test method has been developed to closely control the test parameters with particular regard to dissolved oxygen and pH in order to ensure consistency of results. The test results will be presented and the SSC performance of the material will be discussed with consideration to the test temperature pH partial pressure of H2S and surface condition of the specimens.
 

Product tags
Also Purchased
Picture for Sour Service Limits of Martensitic SS: Review of Current Knowledge Test Methods and Development
Available for download

51313-02639-Sour Service Limits of Martensitic SS: Review of Current Knowledge Test Methods and Development

Product Number: 51313-02639-SG
ISBN: 02639 2013 CP
Author: Nacéra Sabrina Meck
Publication Date: 2013
$20.00
Picture for Evaluating Inhibitor Performance in CO2-Saturated Erosion-Corrosion Environments
Available for download

51313-02585-Evaluating Inhibitor Performance in CO2-Saturated Erosion-Corrosion Environments

Product Number: 51313-02585-SG
ISBN: 02585 2013 CP
Author: Richard Barker
Publication Date: 2013
$20.00
Picture for Development of Sour Service Offshore High Strength and Heavy Wall Line Pipe DSAW Process
Available for download

51313-02580-Development of Sour Service Offshore High Strength and Heavy Wall Line Pipe DSAW Process

Product Number: 51313-02580-SG
ISBN: 02580 2013 CP
Author: Tribhuwan Kathayat
Publication Date: 2013
$20.00
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support