Evaluation of Preferential Weld Corrosion Susceptibility and Its Mitigation in Slightly Sour Conditions

Picture for Evaluation of Preferential Weld Corrosion Susceptibility and Its Mitigation in Slightly Sour Conditions
Available for download

Preferential Weld Corrosion (PWC) susceptibility was studied in a slightly sour wet gas piping system using electrochemical methods based on the “hockey puck” technique. Several corrosion inhibitors were evaluated to assess their performance in suppressing PWC.

Product Number: 51315-5640-SG
ISBN: 5640 2015 CP
Author: Ray Case
Publication Date: 2015
Industry: Chemical Inhibitors
$0.00
$20.00
$20.00

Preferential Weld Corrosion (PWC) susceptibility was studied in slightly sour wet gas piping system using electrochemical methods based on the “hockey puck” technique. By establishing a benchmark testing environment that simulates the operating conditions several corrosion inhibitors were evaluated to assess their performance in suppressing PWC in static conditions.The results show that under the testing conditions the Heat Affected Zones (HAZ) from the welds are susceptible to PWC. Also pitting occurs across all the components of the weld independently of the relative cathode / anode relationship. Profilometry assessment of the specimen after exposure supports the findings from the electrochemical measurements. The corrosion inhibitors dosed at 100 ppm concentration in static conditions show reduction of PWC and pitting severity.

Keywords: Conference Papers, conference Papers 2015, preferenctial weld corrosion, Inhibitors, electrochemical

Preferential Weld Corrosion (PWC) susceptibility was studied in slightly sour wet gas piping system using electrochemical methods based on the “hockey puck” technique. By establishing a benchmark testing environment that simulates the operating conditions several corrosion inhibitors were evaluated to assess their performance in suppressing PWC in static conditions.The results show that under the testing conditions the Heat Affected Zones (HAZ) from the welds are susceptible to PWC. Also pitting occurs across all the components of the weld independently of the relative cathode / anode relationship. Profilometry assessment of the specimen after exposure supports the findings from the electrochemical measurements. The corrosion inhibitors dosed at 100 ppm concentration in static conditions show reduction of PWC and pitting severity.

Keywords: Conference Papers, conference Papers 2015, preferenctial weld corrosion, Inhibitors, electrochemical

Product tags
Also Purchased
Picture for 05277 Preferential Weld Corrosion: Effects of
Available for download

05277 Preferential Weld Corrosion: Effects of Weldment Microstructure and Composition

Product Number: 51300-05277-SG
ISBN: 05277 2005 CP
Author: Chi-Ming Lee and Paul Woollin, TWI Ltd.
$20.00
Picture for Evaluation of Corrosion Inhibitor Functionality on the Mitigation of Preferential Weld Corrosion
Available for download

51318-10965-Evaluation of Corrosion Inhibitor Functionality on the Mitigation of Preferential Weld Corrosion

Product Number: 51318-10965-SG
Author: R. Barson / D. D. Korwin-Kochanowski / S. Turgoose / G. Economopoulos / G. E. Dicken
Publication Date: 2018
$20.00

The work conducted produced conditions where preferential weld corrosion initiated in uninhibited conditions and was sustained throughout inhibition. Two types of weld metallurgies; one weld consumable with 1% nickel, the second matched the parent pipe.
Picture for 11268 Control of Preferential Weld Corrosion of X65 Pipeline Steel in Flowing Brines
Available for download

11268 Control of Preferential Weld Corrosion of X65 Pipeline Steel in Flowing Brines Containing Carbon Dioxide

Product Number: 51300-11268-SG
ISBN: 11268 2011 CP
Author: Mylene Martinez, Khaled Alawadhi, Michael Robinson, Graham Nelson and Andrew MacDonald
Publication Date: 2011
$20.00
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support