51318-10918-Control of Corrosion Inhibitor Fouling in Highly Sour System

Picture for Control of Corrosion Inhibitor Fouling in Highly Sour System
Available for download

Black tar-like fouling material was driving frequent shut-downs of a gas plant. Analysis indicated that the nitrogen containing corrosion inhibitor (CI) polymerized with sulfur compounds in a vulcanization process. Testing confirmed the role of the CI in creating this fouling.

Product Number: 51318-10918-SG
Author: Sonja Richter / Jay Locklear / Mohsen Achour / Thomas Baugh / Probjot Singh / Ross Goff
Publication Date: 2018
Industry: Petroleum Refining
$0.00
$20.00
$20.00

Black tar-like fouling material was driving frequent shut-downs and increasing corrosion in the inlet area of a gas plant that processes lean gas with high acid gas content (68%CH4, 20%CO2 and 12%H2S). Analytical work indicated that the nitrogen containing corrosion inhibitor (CI) polymerized with sulfur compounds (polysulfides, elemental sulfur and/or H2S) in a type of a vulcanization process resulting in a hard-to-clean insoluble fouling product. Corrosion testing confirmed the role of the CI in creating this fouling. A customized autoclave testing was designed to include powdered elemental sulfur circulating in the bulk fluid. This allowed for a recreation of the condition in the plant where solid elemental sulfur comes out of solution and fouling occurs. The tests reproduced the tar-like fouling substance in the presence of the incumbent corrosion inhibitor. The data showed that a surfactant (wetting agent) used to keep elemental sulfur from depositing would also protect the steel from elemental sulfur corrosion. Other CIs were tested, but none provided protection at an acceptable dosage level without forming this foulant material.

Key words: sour corrosion, H2S, corrosion inhibitor, fouling, autoclave testing, elemental sulfur

Black tar-like fouling material was driving frequent shut-downs and increasing corrosion in the inlet area of a gas plant that processes lean gas with high acid gas content (68%CH4, 20%CO2 and 12%H2S). Analytical work indicated that the nitrogen containing corrosion inhibitor (CI) polymerized with sulfur compounds (polysulfides, elemental sulfur and/or H2S) in a type of a vulcanization process resulting in a hard-to-clean insoluble fouling product. Corrosion testing confirmed the role of the CI in creating this fouling. A customized autoclave testing was designed to include powdered elemental sulfur circulating in the bulk fluid. This allowed for a recreation of the condition in the plant where solid elemental sulfur comes out of solution and fouling occurs. The tests reproduced the tar-like fouling substance in the presence of the incumbent corrosion inhibitor. The data showed that a surfactant (wetting agent) used to keep elemental sulfur from depositing would also protect the steel from elemental sulfur corrosion. Other CIs were tested, but none provided protection at an acceptable dosage level without forming this foulant material.

Key words: sour corrosion, H2S, corrosion inhibitor, fouling, autoclave testing, elemental sulfur

Product tags
Also Purchased
Picture for High Temperature Alloys Failures in the Petrochemical Furnaces. Mitigation and Prevention
Available for download

51318-10877-High Temperature Alloys Failures in the Petrochemical Furnaces. Mitigation and Prevention

Product Number: 51318-10877-SG
Author: Ali H. AlShawaf / Manabendra K. Maity
Publication Date: 2018
$20.00

This paper explains the most common damage mechanisms of high temperature alloys in radiant section such as creep/carburization, thermal fatigue/carburization, and thermal shock.

 
Picture for The Development of Corrosion Monitoring Techniques for Maintenance Management in Petrochemical Plant
Available for download

51318-10629-The Development of Corrosion Monitoring Techniques for Maintenance Management in Petrochemical Plant

Product Number: 51318-10629-SG
Author: Takao Ohtsu / Masazumi Miyazawa
Publication Date: 2018
$20.00

A developed monitoring approach confirmed that the EN-based electrochemical surveillance can detect changes in a petrochemical plant that otherwise could lead to catastrophic failure.
Marta A. Zuflacht, Erica N. Macha, Jessica Coogan, James F. Dante
Available for download

51318-10915-Analysis of Corrosion Damage on Samples Exposed to Accelerated and Outdoor Corrosion Environments

Product Number: 51318-10915-SG
Author: Marta A. Zuflacht, Erica N. Macha, Jessica Coogan, James F. Dante
Publication Date: 2018
$20.00

Quantitative analysis of the corrosion morphology after accelerated testing and outdoor exposures of lapjoint test panels coupled with various fastener materials. Image analysis of 3-D microscope images was used to quantify average depth of attack and percent surface area damage.
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support