The crack growth kinetics and solution chemistry developed within environment-assisted cracks (EAC) grown in laboratory tests and long-term field exposures of high-strength A1-Zn-Mg-Cu alloys were assessed. For both test programs, peak-aged (T651) material exhibited crack growth kinetics...
Keywords: aluminum alloy, 7xxx series, environment-assisted cracking, crack chemistry, field-testing