97033 PERFORMANCE OF CRA IN CONCENTRATED BRINES AT 130° TO 180°C - EFFECT OF H2S ELEMENTAL SULFUR AND BRINE COMPOSITION

Picture for 97033 PERFORMANCE OF CRA IN CONCENTRATED
Available for download
Product Number: 51300-97033-SG
ISBN: 97033 1997 CP
Author: W. Bruckhoff, G. Siegmund, G.Schmitt, U. Pankoka, G. Klemp
$0.00
$20.00
$20.00
Failure analysis of localised corrosion at 28 Cr32Ni (Alloy 28) tubing in a sour gas well prompted systematic investigations on the performance of relevant corrosion resistant alloys (CRA) in synthetic high salinity brines at high H2S partial pressures in the absence and presence of elemental sulfur at 130° to 180°C. The CRAS included superaustenitic steels, nickel and nickel-cobalt base alloys and titanium alloys. CRAS with pitting resistance equivalents (PRE)of 39 and lower (including 28 Cr32Ni) suffered in unbuffered brines from pitting and crevice corrosion already at 130°C. Alloy C276 and Ti Beta-C alloys proved complete resistance in all media tested up to 180° C. The effect of medium composition on CRA performance was studied at 130°C with respect to the presence of elemental sulfur, H2S, iron sulfide, and CaCO3 in NaCl/CaCl2 brines with a total of 160 g/l chloride. Keywords: Sour gas, gas well, corrosion. resistant alloys, austenitic steels, nickel base alloys, nickel-cobalt base alloy, titanium alloys, hydrogen sulfide, elemental sulfur, brine, sodium chloride, calcium chloride, calcium carbonate, buffer, iron sulfides.
Failure analysis of localised corrosion at 28 Cr32Ni (Alloy 28) tubing in a sour gas well prompted systematic investigations on the performance of relevant corrosion resistant alloys (CRA) in synthetic high salinity brines at high H2S partial pressures in the absence and presence of elemental sulfur at 130° to 180°C. The CRAS included superaustenitic steels, nickel and nickel-cobalt base alloys and titanium alloys. CRAS with pitting resistance equivalents (PRE)of 39 and lower (including 28 Cr32Ni) suffered in unbuffered brines from pitting and crevice corrosion already at 130°C. Alloy C276 and Ti Beta-C alloys proved complete resistance in all media tested up to 180° C. The effect of medium composition on CRA performance was studied at 130°C with respect to the presence of elemental sulfur, H2S, iron sulfide, and CaCO3 in NaCl/CaCl2 brines with a total of 160 g/l chloride. Keywords: Sour gas, gas well, corrosion. resistant alloys, austenitic steels, nickel base alloys, nickel-cobalt base alloy, titanium alloys, hydrogen sulfide, elemental sulfur, brine, sodium chloride, calcium chloride, calcium carbonate, buffer, iron sulfides.
PRICE BREAKS - The more you buy, the more you save
Quantity
1+
5+
Price
$20.00
$20.00
Product tags
Also Purchased
Picture for 11123 Performance of Stressed CRAs in Contact with Elemental Sulfur
Available for download

11123 Performance of Stressed CRAs in Contact with Elemental Sulfur in Highly Sour Brine

Product Number: 51300-11123-SG
ISBN: 2011 11123 CP
Author: Guenter Schmitt, Gerit Siegmund, Josef Noga
Publication Date: 2011
$20.00
Picture for 11398 Investigation of Elemental Sulfur Corrosion Mechanisms
Available for download

11398 Investigation of Elemental Sulfur Corrosion Mechanisms

Product Number: 51300-11398-SG
ISBN: 2011 11398 CP
Author: Haitao Fang, Bruce Brown, David Young, Srdjan Nešic
Publication Date: 2011
$20.00
Picture for Interactive effects of H2S and elemental sulfur on corrosion of steel
Available for download

51312-01575-Interactive effects of H2S and elemental sulfur on corrosion of steel

Product Number: 51312-01575-SG
ISBN: 01575 2012 CP
Author: Lei Zhang
Publication Date: 2012
$20.00
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support