01643 Improving the Damage Tolerance, and Extending the Service Life of Fusion-Bonded Epoxy Coatings

Product Number: 51300-01643-SG
ISBN: 01643 2001 CP
Author: D.G. Enos, J.A. Kehr, C.R. Guilbert
$0.00
$20.00
$20.00
Today, the traditional fusion-bonded epoxy (FBE) coatings used to protect carbon steel reinforcing bar (rebar) and pipe are being placed under increased scrutiny. Concerns have been raised which question the ability of such coatings to abate corrosion in the long term. Researchers have argued that a damaged, FBE coated rebar exhibits poorer corrosion performance than a comparable uncoated, black steel rebar. This reduced corrosion performance and corresponding service life is likely the result of local anodic sites which develop along the coated rebar or pipe in areas where the FBE coating has been removed due to impact or abrasion. A novel coating design has been developed, the implementation of which significantly improves the damage tolerance of epoxy coated components in a variety of high chloride environments, such as an aging concrete bridge deck. In this study, the coating was successfully applied using conventional electrostatic-spray equipment at a commercial applicator. The resulting coated rebar was able to exceed the performance requirements of a coat-after-fabrication application in terms of cathodic delamination. This paper details the results achieved to date, as well as outlining the in-concrete test program currently underway. Keywords: Fusion-Bonded Epoxy, FBE, ECR, FBECR, Corrosion, Concrete, Rebar, Steel, Microencapsulation, Inhibitor
Today, the traditional fusion-bonded epoxy (FBE) coatings used to protect carbon steel reinforcing bar (rebar) and pipe are being placed under increased scrutiny. Concerns have been raised which question the ability of such coatings to abate corrosion in the long term. Researchers have argued that a damaged, FBE coated rebar exhibits poorer corrosion performance than a comparable uncoated, black steel rebar. This reduced corrosion performance and corresponding service life is likely the result of local anodic sites which develop along the coated rebar or pipe in areas where the FBE coating has been removed due to impact or abrasion. A novel coating design has been developed, the implementation of which significantly improves the damage tolerance of epoxy coated components in a variety of high chloride environments, such as an aging concrete bridge deck. In this study, the coating was successfully applied using conventional electrostatic-spray equipment at a commercial applicator. The resulting coated rebar was able to exceed the performance requirements of a coat-after-fabrication application in terms of cathodic delamination. This paper details the results achieved to date, as well as outlining the in-concrete test program currently underway. Keywords: Fusion-Bonded Epoxy, FBE, ECR, FBECR, Corrosion, Concrete, Rebar, Steel, Microencapsulation, Inhibitor
PRICE BREAKS - The more you buy, the more you save
Quantity
1+
5+
Price
$20.00
$20.00
Product tags
Also Purchased
Picture for 00168 PERFORMANCE TESTING OF
FUSION BONDED
Available for download

00168 PERFORMANCE TESTING OF FUSION BONDED EPOXY COATINGS

Product Number: 51300-00168-SG
ISBN: 00168 2000 CP
Author: Joe H. Payer, Douglas P. Moore, J. Lee Magnon
$20.00
Picture for 08037 Review of Epoxy Polymer Thermal Aging Behavior Relevant to Fusion Bonded Epoxy Coatings
Available for download

08037 Review of Epoxy Polymer Thermal Aging Behavior Relevant to Fusion Bonded Epoxy Coatings

Product Number: 51300-08037-SG
ISBN: 08037 2008 CP
Author: Don E. Kirkpatrick, Fabio Aguirre, and George C. Jacob
Publication Date: 2008
$20.00