TM0284-HD2003-SG Evaluation of Pipeline and Pressure Vessel Steels for Resistance to Hydrogen-Induced Cracking-HD2003

Picture for TM0284-Evaluation of Pipeline and Pressure Vessel Steels for Resistance to Hydrogen-Induced Cracking-HD2003
Available for download

This standard establishes a test method for evaluating the resistance of pipeline and pressure vessel plate steels to HIC caused by hydrogen absorption from aqueous sulfide corrosion. Historical Document 2003

Product Number: 21215-HD2003
ISBN: 1-57590-163-3
Author: NACE International
Publication Date: 2003
Industries: Corrosion Monitoring and Control , Test Method
$179.00
$179.00
$179.00

Absorpticcon of hydrogen generated by corrosion of steel in a wet hydrogen sulfide (H2S) environment can have several effects that depend on the properties of the steel, the characteristics of the environment, and other variables. One adverse effect observed in pipeline and pressure vessel steels is the development of cracks along the rolling direction of the .steel. Cracks on one plane tend to link up with the cracks on adjacent planes to form steps across the thickness. The cracks can reduce the effective wall thickness until the pipe or pressure vessel becomes overstressed and ruptures. Cracking is sometimes accompanied by surface blistering. Several service failures attributed to such cracking have been reported.

The terms stepwise cracking (SWC), hydrogen pressure cracking, blister cracking, and hydrogen-induced stepwise cracking have been used in the past to describe cracking of this type in pipeline and pressure vessel steels, but are now considered obsolete. The term hydrogen-induced cracking (HIC) has been widely used for describing cracking of this type, and has been adopted by NACE International. Therefore, it is used throughout this standard test method.

1.1 This standard establishes a test method for evaluating the resistance of pipeline and pressure vessel plate steels to HIC caused by hydrogen absorption from aqueous sulfide corrosion.

Historical Document 2003

Absorpticcon of hydrogen generated by corrosion of steel in a wet hydrogen sulfide (H2S) environment can have several effects that depend on the properties of the steel, the characteristics of the environment, and other variables. One adverse effect observed in pipeline and pressure vessel steels is the development of cracks along the rolling direction of the .steel. Cracks on one plane tend to link up with the cracks on adjacent planes to form steps across the thickness. The cracks can reduce the effective wall thickness until the pipe or pressure vessel becomes overstressed and ruptures. Cracking is sometimes accompanied by surface blistering. Several service failures attributed to such cracking have been reported.

The terms stepwise cracking (SWC), hydrogen pressure cracking, blister cracking, and hydrogen-induced stepwise cracking have been used in the past to describe cracking of this type in pipeline and pressure vessel steels, but are now considered obsolete. The term hydrogen-induced cracking (HIC) has been widely used for describing cracking of this type, and has been adopted by NACE International. Therefore, it is used throughout this standard test method.

1.1 This standard establishes a test method for evaluating the resistance of pipeline and pressure vessel plate steels to HIC caused by hydrogen absorption from aqueous sulfide corrosion.

Historical Document 2003

Product tags
Also Purchased
Picture for NACE RP0495-2003
Available for download

NACE RP0495-2003, Guidelines for Qualifying Personnel as Abrasive Blasters and Coating and Lining Applicators in the Rail Industries

Product Number: 21072-SG
Publication Date: 2003
$179.00

HISTORICAL DOCUMENT. Training and qualification of craftsmen engaged in abrasive blasting and the application of modern coatings and linings systems.
Picture for SP0394-2013 (formerly RP0394)
Available for download

SP0394-2013 (formerly RP0394), "Application, Performance, and Quality Control of Plant-Applied Single Layer Fusion-Bonded Epoxy External Pipe Coating”

Product Number: 21064-SG
Publication Date: 2013
$179.00

HISTORICAL DOCUMENT. Qualifying and controlling the quality of plant-applied, single-layer fusion-bonded epoxy (FBE) coatings to the external surfaces of carbon steel pipe.  Proper application,  inspection and repair.

NOTE: NACE SP0394-2013—Editorial corrections were made to Table 3 and Table 4 in 2018-04-04. 
Picture for SP0196-2015
Available for download

SP0196-2015 (formerly RP0196), “Galvanic Anode Cathodic Protection of Internal Submerged Surfaces of Steel Water Storage Tanks”

Product Number: 21077-SG
ISBN: 1-57590-189-7
Publication Date: 2015
$179.00

HISTORICAL DOCUMENT. Galvanic anode cathodic protection (CP) for submerged steel surfaces in water supply and fire protection storage tanks.  Design and installation of CP systems.  Effectiveness evaluation, operation, maintenance. 
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support