The Effect Of Flow Rate On Corrosion Currents From Various Aircraft Primers



Product Number: 51321-16932-SG
Author: James F. Dante
Publication Date: 2021
$0.00
$20.00
$20.00

The functional life of paint in DoD is defined by the barrier properties and protective corrosion inhibiting capacity of the coating system. The time till corrosion initiation of an underlying substrate can thus be defined in general terms as 1) the time for an external environment to reach the coating/substrate interface through coating porosity, coating cracking,  or mechanical damage and 2) inhibitor exhaustion/depletion. In other words, once a coating system has been breached, protection is afforded by the availability of inhibitors at the defect site. In this work, the parameters that influence inhibitor exhaustion will be examined. The onset of corrosion at a defect is a function of inhibitor release rate, the ratio of inhibitor to aggressive ions, and consumption of inhibitor in the vicinity of the defect. In this paper, the effect artificial inhibitor consumption on corrosion rate through the use of a flowing cell and a Multi-electrode Array probe will specifically be explored. The effect of flow rate on corrosion current will be shown for three different military primer systems. Steady state inhibitor concentrations at each flow rate will be used to explain the individual effects of flow and chromate content on corrosion current.

The functional life of paint in DoD is defined by the barrier properties and protective corrosion inhibiting capacity of the coating system. The time till corrosion initiation of an underlying substrate can thus be defined in general terms as 1) the time for an external environment to reach the coating/substrate interface through coating porosity, coating cracking,  or mechanical damage and 2) inhibitor exhaustion/depletion. In other words, once a coating system has been breached, protection is afforded by the availability of inhibitors at the defect site. In this work, the parameters that influence inhibitor exhaustion will be examined. The onset of corrosion at a defect is a function of inhibitor release rate, the ratio of inhibitor to aggressive ions, and consumption of inhibitor in the vicinity of the defect. In this paper, the effect artificial inhibitor consumption on corrosion rate through the use of a flowing cell and a Multi-electrode Array probe will specifically be explored. The effect of flow rate on corrosion current will be shown for three different military primer systems. Steady state inhibitor concentrations at each flow rate will be used to explain the individual effects of flow and chromate content on corrosion current.

Also Purchased
Picture for 01624 Corrosion Rate and Severity Results from
Available for download

01624 Corrosion Rate and Severity Results from In-Line-Inspection Data

Product Number: 51300-01624-SG
ISBN: 01624 2001 CP
Author: Guy Desjardins
$20.00
Picture for 00405 AN ADVANCED ATMOSPHERIC CORROSION
Available for download

00405 AN ADVANCED ATMOSPHERIC CORROSION MEASUREMENT SYSTEM

Product Number: 51300-00405-SG
ISBN: 00405 2000 CP
Author: Philippe Kempe, Allen Denzine, and Eugen Tiefnig
$20.00
Picture for 00356 EFFECTS OF O2 AND CO2 ON NEAR-NEUTRAL-pH
Available for download

00356 EFFECTS OF O2 AND CO2 ON NEAR-NEUTRAL-pH STRESS CORROSION CRACK PROPAGATION

Product Number: 51300-00356-SG
ISBN: 00356 2000 CP
Author: J. T. Johnson, C. L. Durr, J. A. Beavers, B. S. Delanty
$20.00