51314-4432-The Effect of Chromium Content on the Hot Corrosion Resistance of Nickel Chromium Alloys in Molten Sodium Sulfate

Picture for The Effect of Chromium Content on the Hot Corrosion Resistance of Nickel Chromium Alloys in Molten S
Available for download
Product Number: 51314-4432-SG
ISBN: 4432 2014 CP
Author: Vilupanur Ravi
Publication Date: 2014
$0.00
$20.00
$20.00
The corrosion of metallic alloys underneath fused salt films (“hot corrosion”) is an important degradation problem.  Chromium is a key alloying element in defending against hot corrosion because of its ability to form a protective adherent oxide layer. The role of chromium in the hot corrosion resistance of binary nickel-chromium alloys exposed to molten sodium sulfate was studied by systematically varying the chromium content of the alloys. Alloy samples were immersed in the molten salt for different times at 900C and weight loss data were obtained. These results were compared with those obtained from coating samples with a thin salt film and subsequently exposing them to air at high temperatures.  Microstructural analysis of the corrosion front  and the kinetics of the corrosion process obtained by both techniques will be reported.  The current status of electrochemical tests will be presented as well.
The corrosion of metallic alloys underneath fused salt films (“hot corrosion”) is an important degradation problem.  Chromium is a key alloying element in defending against hot corrosion because of its ability to form a protective adherent oxide layer. The role of chromium in the hot corrosion resistance of binary nickel-chromium alloys exposed to molten sodium sulfate was studied by systematically varying the chromium content of the alloys. Alloy samples were immersed in the molten salt for different times at 900C and weight loss data were obtained. These results were compared with those obtained from coating samples with a thin salt film and subsequently exposing them to air at high temperatures.  Microstructural analysis of the corrosion front  and the kinetics of the corrosion process obtained by both techniques will be reported.  The current status of electrochemical tests will be presented as well.
Product tags
Also Purchased
Picture for Hot Corrosion of Nickel-Chromium Alloys in a Molten Eutectic Salt Environment
Available for download

51316-7824-Hot Corrosion of Nickel-Chromium Alloys in a Molten Eutectic Salt Environment

Product Number: 51316-7824-SG
ISBN: 7824 2016 CP
Author: Vilupanur Ravi
Publication Date: 2016
$20.00
Picture for Corrosion of High Entropy Alloys in Molten Salts
Available for download

51318-11664-Corrosion of High Entropy Alloys in Molten Salts

Product Number: 51318-11664-SG
Author: Alexander Jalbuena / Jared Logier / J. C. Nava / Vilupanur Ravi / Shaik Adil / B.S Murty
Publication Date: 2018
$20.00

Coupons of a multicomponent AlCoCrFeNi alloy and selected nickel-based alloys were exposed to a molten NaCl-Na2SO4 eutectic salt mixture at 700°C in the presence of a platinum-catalyzed SO2/air mixture.
Picture for Aluminide Coatings for Austenitic Stainless Steels
Available for download

51314-4327-Aluminide Coatings for Austenitic Stainless Steels

Product Number: 51314-4327-SG
ISBN: 4327 2014 CP
Author: Vilupanur Ravi
Publication Date: 2014
$0.00
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support