51313-02411-SCC in PWR Water of Alloy 690 and Its Weld Metals

Picture for SCC in PWR Water of Alloy 690 and Its Weld Metals
Available for download
Product Number: 51313-02411-SG
ISBN: 02411 2013 CP
Author: Peter Andresen
Publication Date: 2013
$0.00
$20.00
$20.00

SCC growth rate testing of Alloy 690 base metal HAZ and weld metal has been performed in representative PWR primary water at 290 to 360 C. Intergranular crack growth rates as high as 1.2 x 10–6 mm/s were observed in the S-L orientation with microstructural banded material after cold rolling or forging to align the planes of banding rolling and cracking. Growth rates on homogeneous Alloy 690 including extruded CRDM tubing often approached 10–7 mm/s in cold worked condition and an S-L orientation. Much lower growth rates in some Alloy 690 tests were observed primarily in orientations other than S-L. Alloy 152/52/52i weld metals always exhibited low growth rates apart from a weld that was further cold worked by 20%. Crack growth rates along a carbon steel - 152M interface were very high at ~2 x 10-7 mm/s.
 

SCC growth rate testing of Alloy 690 base metal HAZ and weld metal has been performed in representative PWR primary water at 290 to 360 C. Intergranular crack growth rates as high as 1.2 x 10–6 mm/s were observed in the S-L orientation with microstructural banded material after cold rolling or forging to align the planes of banding rolling and cracking. Growth rates on homogeneous Alloy 690 including extruded CRDM tubing often approached 10–7 mm/s in cold worked condition and an S-L orientation. Much lower growth rates in some Alloy 690 tests were observed primarily in orientations other than S-L. Alloy 152/52/52i weld metals always exhibited low growth rates apart from a weld that was further cold worked by 20%. Crack growth rates along a carbon steel - 152M interface were very high at ~2 x 10-7 mm/s.
 

Product tags
Also Purchased
Picture for SCC of Alloy 825 High Cr Alloy 800 and Other Interesting Alloys in High-Temperature Water
Available for download

51313-02412-SCC of Alloy 825 High Cr Alloy 800 and Other Interesting Alloys in High-Temperature Water

Product Number: 51313-02412-SG
ISBN: 02412 2013 CP
Author: Peter Andresen
Publication Date: 2013
$20.00
Picture for Electrochemical Study and Modeling of H2S Corrosion of Mild Steel
Available for download

51313-02406-Electrochemical Study and Modeling of H2S Corrosion of Mild Steel

Product Number: 51313-02406-SG
ISBN: 02406 2013 CP
Author: Yougui Zheng
Publication Date: 2013
$20.00
Picture for Failure Analysis in a Six Inch Nitrogen Pipeline in Monterrey Mexico
Available for download

51313-02403-Failure Analysis in a Six Inch Nitrogen Pipeline in Monterrey Mexico

Product Number: 51313-02403-SG
ISBN: 02403 2013 CP
Author: Hernan Rivera
Publication Date: 2013
$20.00
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support