Performance of Thermally Sprayed Corrosion Resistant Alloy (CRA) Coatings in 50MPa Supercritical CO2

Picture for Performance of Thermally Sprayed Corrosion Resistant Alloy (CRA) Coatings in 50MPa Supercritical CO2
Available for download

This paper reports the performance of HVOF-sprayed corrosion resistant alloy (CRA) coatings in an aqueous solution bubbled with 50MPa supercritical CO2.

Product Number: 51317--9007-SG
ISBN: 9007 2017 CP
Author: Shiladitya Paul
Publication Date: 2017
Industry: Coatings and Linings
$0.00
$20.00
$20.00

This paper reports the performance of HVOF-sprayed corrosion resistant alloy (CRA) coatings in an aqueous solution bubbled with 50MPa supercritical CO2. 316L stainless steel alloy C-276 and alloy 625 were procured in power form and sprayed onto carbon steel with a JP500 HVOF system and 8 mm holidays were drilled in the coating to expose the steel substrate. These were then exposed to 3.5 wt.% NaCl solution for 30 days bubbled with 50MPa CO2. Tests were conducted at 40°C. Post-test microstructural characterization revealed that the coatings protected the steel substrate from CO2 corrosion when intact. The bare steel in the exposed region formed a siderite scale while no such scale was seen in the undamaged regions. The substrate close to the coating showed accelerated corrosion due to galvanic effects. It can be concluded that thermally sprayed CRA coatings are a candidate to provide cost-effective corrosion mitigation in wet supercritical CO2. However care must be taken to ensure that the thermally sprayed CRA layer does not have any through porosity or damage; else such coatings may accelerate corrosion of the underlying steel due to galvanic interactions.

Keywords: Supercritical CO2, Corrosion resistant coatings, Thermal spray coatings, HVOF Coatings, igh pressure CO2, Dense Phase CO2

This paper reports the performance of HVOF-sprayed corrosion resistant alloy (CRA) coatings in an aqueous solution bubbled with 50MPa supercritical CO2. 316L stainless steel alloy C-276 and alloy 625 were procured in power form and sprayed onto carbon steel with a JP500 HVOF system and 8 mm holidays were drilled in the coating to expose the steel substrate. These were then exposed to 3.5 wt.% NaCl solution for 30 days bubbled with 50MPa CO2. Tests were conducted at 40°C. Post-test microstructural characterization revealed that the coatings protected the steel substrate from CO2 corrosion when intact. The bare steel in the exposed region formed a siderite scale while no such scale was seen in the undamaged regions. The substrate close to the coating showed accelerated corrosion due to galvanic effects. It can be concluded that thermally sprayed CRA coatings are a candidate to provide cost-effective corrosion mitigation in wet supercritical CO2. However care must be taken to ensure that the thermally sprayed CRA layer does not have any through porosity or damage; else such coatings may accelerate corrosion of the underlying steel due to galvanic interactions.

Keywords: Supercritical CO2, Corrosion resistant coatings, Thermal spray coatings, HVOF Coatings, igh pressure CO2, Dense Phase CO2

Product tags
Also Purchased
Picture for Corrosion Inhibition of Pipeline Steels Under Supercritical CO2 Environment
Available for download

Corrosion Inhibition of Pipeline Steels Under Supercritical CO2 Environment

Product Number: 51317--9153-SG
ISBN: 9153 2017 CP
Author: Yoon-Seok Choi
Publication Date: 2017
$20.00

In the present study, the performance of imidazoline-based corrosion inhibitor was evaluated by examining environmental effects on the corrosion rate and corrosion behavior of materials.
Picture for The Effect of High Partial Pressure of CO2 on the Corrosion Mechanism of Carbon Steel in H2O-CO2 Systems
Available for download

51318-11623-The Effect of High Partial Pressure of CO2 on the Corrosion Mechanism of Carbon Steel in H2O-CO2 Systems

Product Number: 51318-11623-SG
Author: Tatiana C. Almeida / Oscar R. Mattos / Rogaciano M. Moreira / Merlin C. E. Bandeira
Publication Date: 2018
$20.00

The corrosion mechanism of X65 carbon steel was evaluated in water environment by increasing CO2 partial pressure from 1 bar at 24 °C to 110 bar at 40 °C, reaching conditions that include water saturated with supercritical CO2.
Picture for 03345 CORROSION AT HIGH CO2 PRESSURE
Available for download

03345 CORROSION AT HIGH CO2 PRESSURE

Product Number: 51300-03345-SG
ISBN: 03345 2003 CP
Author: S. M. Hesjevik, S. Olsen, Statoil, Marion Seiersten
$20.00
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support