Metal Dusting Resistance Of Nicrmocu Alloy And Its Weld Overlay Under High Pressure Condition

Picture for Metal Dusting Resistance Of Nicrmocu Alloy And Its Weld Overlay Under High Pressure Condition
Available for download

Many industrial processes contain H2, CO, CO2, and H2O gas mixtures, such as syngas production and processing in hydrogen, ammonia, and methanol plants. These process environments have high carbon activity, i.e. ac > 1, and low oxygen partial pressure at their elevated operating temperatures, such as in the temperature range of 400-800 °C (752-1472 °F). The high carbon activity could result in a catastrophic material degradation, i.e. metal dusting. The resulting corrosion products consist of carbon or graphite and metal particles, along with possible carbides and oxides, and cause material disintegration.

Product Number: 51322-17570-SG
Author: Bingtao Li, Vinay Deodeshmukh, Clara Schlereth, Anke S. Ulrich, Mathias C. Galetz
Publication Date: 2022
Industries: Corrosion Monitoring and Control , Coatings and Linings , Coatings
$0.00
$20.00
$20.00

A relatively new N06235 alloy has been developed to offer excellent metal dusting resistance by utilizing the effect of copper on inhibiting carbon deposition and graphite formation, and its weld overlay could provide a cost-efficient alternative for metal dusting and other high temperature corrosion protection. The current paper studied metal dusting resistance of the N06235 alloy and its weld overlays, which were applied by Gas Metal Arc Welding (GMAW) or Hot-Wire Laser process on N06230 alloy plate, along with a wrought N06025 alloy for comparison. The metal dusting test was conducted in a 47CO-47H2-2H2O-4CO2 gas with high carbon activity under 18bar pressure at 620°C. The test coupons were periodically removed from the furnace to measure weight change and check on metal dusting attack. After 790h exposure, the N06235 alloy and its weld overlays showed excellent metal dusting resistance, while metal dusting attack was observed on the wrought alloys, N06025 and N06230, after the first 50h exposure. Metallurgical examination after the metal dusting test was performed to characterize the metal dusting attack on the N06235 weld overlay and the wrought alloys N06025 and N06230. Detailed investigation and discussion on the N06235 weld overlays, including oxide scale, surface pit, and subsurface chemistry change, were presented.

A relatively new N06235 alloy has been developed to offer excellent metal dusting resistance by utilizing the effect of copper on inhibiting carbon deposition and graphite formation, and its weld overlay could provide a cost-efficient alternative for metal dusting and other high temperature corrosion protection. The current paper studied metal dusting resistance of the N06235 alloy and its weld overlays, which were applied by Gas Metal Arc Welding (GMAW) or Hot-Wire Laser process on N06230 alloy plate, along with a wrought N06025 alloy for comparison. The metal dusting test was conducted in a 47CO-47H2-2H2O-4CO2 gas with high carbon activity under 18bar pressure at 620°C. The test coupons were periodically removed from the furnace to measure weight change and check on metal dusting attack. After 790h exposure, the N06235 alloy and its weld overlays showed excellent metal dusting resistance, while metal dusting attack was observed on the wrought alloys, N06025 and N06230, after the first 50h exposure. Metallurgical examination after the metal dusting test was performed to characterize the metal dusting attack on the N06235 weld overlay and the wrought alloys N06025 and N06230. Detailed investigation and discussion on the N06235 weld overlays, including oxide scale, surface pit, and subsurface chemistry change, were presented.

Product tags
Also Purchased
Picture for Long-Term Cost Saving By Using High Alloyed Stainless Steel In Seawater Coolers
Available for download

Long-Term Cost Saving By Using High Alloyed Stainless Steel In Seawater Coolers

Product Number: 51322-17544-SG
Author: Jonas Höwing
Publication Date: 2022
$20.00

Copper alloys such as copper nickel (CuNi) and Admiralty Brass (CuZn) are often successful material selections for seawater coolers. The copper alloys successes in these highly corrosive environments can be attributes to the ability of copper to form a protective scale, thus stopping corrosion of the material. On copper alloys in seawater, the protective scale formed comprises a mix of cuprous oxide (Cu2O), copper oxide (CuO) and copper hydroxy chlorides.
Picture for Local Hard Zones On TMCP Large Diameter Line Pipes: What Do We Know?
Available for download

Local Hard Zones On TMCP Large Diameter Line Pipes: What Do We Know?

Product Number: 51322-17565-SG
Author: Hervé Marchebois, Bruce Cowe, Thierry Cassagne
Publication Date: 2022
$20.00

The current paper deals with a thorough analysis of these newly recognized LHZ with Scanning Electron Microscope (SEM) and Electron Back Scattering Diffraction (EBSD) investigations through the wall thickness of pipes. Internal diameter (ID) surface, intermediate zone and bulk metal microstructures showed an increase of a strong misorientation while approaching the ID. Thus, LHZ is characterized by the presence of lath and especially lower bainite type microstructures associated to high local hardness above the NACE MR 0175 / ISO 15156 limits for sour service applications.
Picture for Mechanical, Microstructural And Corrosion Characterization Of Low Binder Containing WC-Co Grades Using A Binderjet Process
Available for download

Mechanical, Microstructural And Corrosion Characterization Of Low Binder Containing WC-Co Grades Using A Binderjet Process

Product Number: 51322-17583-SG
Author: Krutibas Panda, Ed Rusnica, Reece Goldsberry, Jerry Domingue, Paul Prichard, Zhuqing Wang
Publication Date: 2022
$20.00

Cemented carbides have been widely used to make parts for wear applications due to the excellent combination of hardness and toughness. Cemented carbides represent a group of composite materials containing hard metal carbides, such as tungsten carbide (WC), bonded by ductile metallic binder agents, such as cobalt (Co), nickel (Ni), or iron (Fe).1 By varying WC grain size, weight fraction of metallic binder, and processing parameters, a wider range of microstructure and mechanical properties can be achieved.
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support