Impact of Test Method on Sulfide Stress Cracking Fracture Toughness

Picture for Impact of Test Method on Sulfide Stress Cracking Fracture Toughness
Available for download

When dealing with the risk of Sulfide Stress Cracking (SSC) of Oil Country Tubular Goods (OCTG) as casings and tubings, two main approaches are: either the determination of the threshold stress on a smooth tensile specimen (NACE TM0177 Method A) or the fracture toughness KISSC on a Double Cantilever Beam (DCB) specimen (NACE TM0177 Method D).
Relevance of KISSC for predicting the behavior of real pipes in service has been assessed in the frame of API PRAC project Phase II.1 Hollow tensile specimens sampled in the wall of sour service seamless pipes were exposed to sour environments either on Inner Diameter (ID), Outer Diameter (OD) or both and subjected to a tensile loading (see also references

Product Number: 51323-19118-SG
Author: Florian Thebault, Christelle Gomes, Daniela Garcia
Publication Date: 2023
$0.00
$20.00
$20.00

Double Cantilever Beam (DCB) test as per Method D of NACE TM0177 is the most used method for the evaluation of the Sulfide Stress Cracking fracture toughness KISSC. Klimit has been introduced in the latest revision of the standard for suppressing the influence of the wedge thickness on KISSC. Recently, Single Edge Notch Tension (SENT) has been proposed as an alternative geometry for obtaining threshold KISSC values. The present work aims to further compare these two testing methodologies on a C110 in two environments presenting different abilities to hydrogenate the material. Results show that KISSC-SENT tends to be more conservative than Klimit, especially in mild sour environment. This observation is explained by crack arrest versus crack initiation configurations and time-dependent hydrogen absorption inside specimens. This interpretation is strengthened by crack growth resistance curve performed on SENT specimens presenting different surface coating configurations able to delay hydrogen uptake rate.

Double Cantilever Beam (DCB) test as per Method D of NACE TM0177 is the most used method for the evaluation of the Sulfide Stress Cracking fracture toughness KISSC. Klimit has been introduced in the latest revision of the standard for suppressing the influence of the wedge thickness on KISSC. Recently, Single Edge Notch Tension (SENT) has been proposed as an alternative geometry for obtaining threshold KISSC values. The present work aims to further compare these two testing methodologies on a C110 in two environments presenting different abilities to hydrogenate the material. Results show that KISSC-SENT tends to be more conservative than Klimit, especially in mild sour environment. This observation is explained by crack arrest versus crack initiation configurations and time-dependent hydrogen absorption inside specimens. This interpretation is strengthened by crack growth resistance curve performed on SENT specimens presenting different surface coating configurations able to delay hydrogen uptake rate.

Product tags
Also Purchased
Picture for NACE TM0177 Method A High Pressure High Temperature Testing Using Spring-Loaded Sustained Load Windo
Available for download

51316-7581-NACE TM0177 Method A High Pressure High Temperature Testing Using Spring-Loaded Sustained Load Window-Box Fixtures

Product Number: 51316-7581-SG
ISBN: 7581 2016 CP
Author: Sridhar Srinivasan
Publication Date: 2016
$20.00
Picture for Contribution to the Understanding of Hydrogen Stress Cracking Initiation and Propagation in Nickel Based Alloys
Available for download

Contribution to the Understanding of Hydrogen Stress Cracking Initiation and Propagation in Nickel Based Alloys

Product Number: 51323-18873-SG
Author: Bruce Cowe, Flavien Vucko, Hervé Marchebois, Laurent Ponson
Publication Date: 2023
$20.00

This paper presents work in follow-up to the previous study. It is focused on UNS1 N07718, UNS N09925, UNS N07725 and UNS N09946. A series of incremental step load tests of compact tensile specimens were conducted to measure the fracture toughness during testing and cracking was monitored by the Electric Crack Growth Monitoring technique. A new engineering technique, referred to as statistical fractography, was used to investigate the fracture surface morphology and extract from it the fracture properties of the alloys.
Picture for The Performance Tests of HPHT Corrosion Inhibitor at Onshore Downhole Sour Conditions
Available for download

The Performance Tests of HPHT Corrosion Inhibitor at Onshore Downhole Sour Conditions

Product Number: 51323-19242-SG
Author: Heonyeong Song, Kwanghyung Lee, Bang Cha Rang Song, Junpeng Xue
Publication Date: 2023
$20.00

Nowadays, oil and gas fields containing a high concentration of CO2 and H2S at high temperatures are being operated in many areas. Here, internal corrosion control under these conditions has become one of the significant challenges in oil and gas production wells and a major cause of severe corrosion–related material failure in the industry.

Internal corrosion of the pipelines turns out to be a critical threat to the initial stage of production.
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support