51316-7498-Hydrogen Induced Cracking of A516 Plate Steels and the Apparent Effect of Microscopic Banding

Picture for Hydrogen Induced Cracking of A516 Plate Steels and the Apparent Effect of Microscopic Banding
Available for download
Product Number: 51316-7498-SG
ISBN: 7498 2016 CP
Author: Bryan Kulesza
Publication Date: 2016
$0.00
$20.00
$20.00
Several published papers identified microstructural banding as a factor in susceptibility to hydrogen induced cracking (HIC). In the present study over 50 plates from more than 15 heats of A516-70 steel were analyzed for microstructural characteristics including banding index per ASTM E1268 for chemical composition for HIC behavior per NACE TM0284 and for cleanliness rating per ASTM E45. The correlation between HIC behavior and banding index was weak. Scanning Electron Microscopy analyses of opened HIC cracks was used to identify HIC initiation sites. Non-metallic inclusions and untempered martensite were identified as the sources of high CLR values in HIC tested samples. These microstructural characteristics rather than the banding index per se are significant causes of HIC in pressure vessel steels.
Several published papers identified microstructural banding as a factor in susceptibility to hydrogen induced cracking (HIC). In the present study over 50 plates from more than 15 heats of A516-70 steel were analyzed for microstructural characteristics including banding index per ASTM E1268 for chemical composition for HIC behavior per NACE TM0284 and for cleanliness rating per ASTM E45. The correlation between HIC behavior and banding index was weak. Scanning Electron Microscopy analyses of opened HIC cracks was used to identify HIC initiation sites. Non-metallic inclusions and untempered martensite were identified as the sources of high CLR values in HIC tested samples. These microstructural characteristics rather than the banding index per se are significant causes of HIC in pressure vessel steels.
Product tags
Also Purchased
Picture for Hydrogen Induced Cracking of A516 Plate Steels and the Apparent Effect of Microscopic Banding
Available for download

51316-7500-Hydrogen Induced Cracking of A516 Plate Steels and the Apparent Effect of Microscopic Banding

Product Number: 51316-7500-SG
ISBN: 7500 2016 CP
Author: Bryan Kulesza
Publication Date: 2016
$20.00
Picture for 08110 Hydrogen Induced Cracking (HIC) - Laboratory Testing Assessment of Low Alloy Steel Linepipe
Available for download

08110 Hydrogen Induced Cracking (HIC) - Laboratory Testing Assessment of Low Alloy Steel Linepipe

Product Number: 51300-08110-SG
ISBN: 08110 2008 CP
Author: John W. Martin, Jean Kittel, Thierry Cassagne, and Christoph Bosch
Publication Date: 2008
$20.00
Picture for Effect of Microstructure on Hydrogen Induced Cracking and Sulfide Stress Cracking Property of Pressu
Available for download

51312-01204-Effect of Microstructure on Hydrogen Induced Cracking and Sulfide Stress Cracking Property of Pressu

Product Number: 51312-01204-SG
ISBN: 01204 2012 CP
Author: Sung Jin Kim
Publication Date: 2012
$20.00
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support