51318-11557-Failure Analysis of Gas Separator Cooler Tube Leak during service after passing Inspection test duri

Picture for Failure Analysis of Gas Separator Cooler Tube Leak during service after passing Inspection test duri
Available for download

Investigation revealed an erroneous selection of Incoloy 800 material for the gas separator tube instead of Inconel 625 and Incoloy 825 which have shown excellent pitting corrosion resistance.

Product Number: 51318-11557-SG
Author: Mohamud M. Farah / Muazu Mohammed
Publication Date: 2018
Industry: Materials Selection and Design
$0.00
$20.00
$20.00

Failure analysis is performed by most companies in the oil and gas industries; to identify the cause of failure and to institute mitigation strategy to avoid any future occurrence. Localised corrosion is one of the difficult damage mechanisms to manage in the oil and gas sector, material selection is often used as mitigation against this threat. Generally most Nickel-based alloys have shown excellent pitting corrosion resistance and good mechanical properties for extended service; these are selected for services where localised corrosion such as pitting corrosion threat is predicted on case by case basis. There are variance of Nickel-based alloys with different critical pitting temperature (CPT) and despite its superior performance compared to many other corrosion-resistant alloys (CRA), some of these alloys are prone to localised corrosion such as pitting and crevice corrosion.

As expected during normal operation, the wet gas from a HP Separator goes into a Suction Scrubber via the cooler where the temperature is cooled after coming out from the outlet of the compressor. Following a shut down the cooler was inspected with Eddy current and no defect was noted, however after start of the platform a tubed side of the gas cooler leaked into the cooling medium.

This paper presents findings of the failure analysis report. Subsequent investigation revealed an erroneous selection of Incoloy 800 material for the gas separator tube instead of Inconel 625 and Incoloy 825 which have shown excellent pitting corrosion resistance, the mechanism of damage was investigated, and recommendation from the conclusion has been proffered.

Key words: [CPT, CRA, Pitting corrosion, Crevice corrosion, Incoloy 800, 825, Inconel 625.]

Failure analysis is performed by most companies in the oil and gas industries; to identify the cause of failure and to institute mitigation strategy to avoid any future occurrence. Localised corrosion is one of the difficult damage mechanisms to manage in the oil and gas sector, material selection is often used as mitigation against this threat. Generally most Nickel-based alloys have shown excellent pitting corrosion resistance and good mechanical properties for extended service; these are selected for services where localised corrosion such as pitting corrosion threat is predicted on case by case basis. There are variance of Nickel-based alloys with different critical pitting temperature (CPT) and despite its superior performance compared to many other corrosion-resistant alloys (CRA), some of these alloys are prone to localised corrosion such as pitting and crevice corrosion.

As expected during normal operation, the wet gas from a HP Separator goes into a Suction Scrubber via the cooler where the temperature is cooled after coming out from the outlet of the compressor. Following a shut down the cooler was inspected with Eddy current and no defect was noted, however after start of the platform a tubed side of the gas cooler leaked into the cooling medium.

This paper presents findings of the failure analysis report. Subsequent investigation revealed an erroneous selection of Incoloy 800 material for the gas separator tube instead of Inconel 625 and Incoloy 825 which have shown excellent pitting corrosion resistance, the mechanism of damage was investigated, and recommendation from the conclusion has been proffered.

Key words: [CPT, CRA, Pitting corrosion, Crevice corrosion, Incoloy 800, 825, Inconel 625.]

Product tags
Also Purchased
Picture for 51318-11549- Comparison of Corrosion resistance of HVOF tungsten carbide & Inconel 625 Coating on ENP coated carbon steel in inhibited HCI solutions
Available for download

51318-11549- Comparison of Corrosion resistance of HVOF tungsten carbide & Inconel 625 Coating on ENP coated carbon steel in inhibited HCI solutions

Product Number: 51318-11549-SG
Author: Hojatollah Almasi / Ahmad Kamali / Fatemeh Namazi / Rahele Jafari
Publication Date: 2018
$20.00

This study investigates corrosion of carbon steel balls and the valve seat during acid cleaning in inhibited HCL_1_ solution.
Picture for New Design/Material Solution for Pipeline Chemicals and Permeation
Available for download

51318-11559-New Design/Material Solution for Pipeline Chemicals and Permeation

Product Number: 51318-11559-SG
$20.00

Results of both laboratory testing and field evaluation will display the performance weaknesses of glass reinforced epoxy (GRE) gaskets.  A newly developed technological solution for pipelines requiring isolation will be presented.
Picture for Pitting Corrosion Resistance of a 316L Stainless Steel Manufactured by the Direct Metal Laser Sintering Process
Available for download

51318-11569-Pitting Corrosion Resistance of a 316L Stainless Steel Manufactured by the Direct Metal Laser Sintering Process

Product Number: 51318-11569-SG
Author: C. Prieto / D. Young / M. Singer / M. Clum / T. J. Cyders
Publication Date: 2018
$20.00

Evaluation of the pitting corrosion resistance of 316L stainless steel manufactured using direct metal laser sintering (DMLS). Rolled 316L stainless steel specimens with similar chemical composition were used as a reference.

 
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support