51316-7272-Electrochemical Study of Nb-10Ta-1Re and Ti-6Al-4V Alloys for Dental Implant Applications

Picture for Electrochemical Study of Nb-10Ta-1Re and Ti-6Al-4V Alloys for Dental Implant Applications
Available for download

Dental implants are exposed to a wide range of pH values of saliva and different concentrations of fluoride. In this study, the effects of fluoride concentration and pH value on the corrosion behavior of Nb-10Ta-1Re and Ti-6Al-4V alloys in artificial saliva at 37°C were investigated by electrochemical measurements.

Product Number: 51316-7272-SG
ISBN: 7272 2016 CP
Author: Wei Wang
Publication Date: 2016
Industries: Materials Selection and Design , Science of Corrosion
$0.00
$20.00
$20.00

Dental implants are exposed to a wide range of pH values of saliva and different concentrations of fluoride. In order to prevent plaque and caries formation, prophylactic products have been used more commonly for dental treatments. These products contain different concentrations of fluoride, for example; bucal rinses, toothpastes and gels contain 200ppm, 1000-1500 ppm and 10000-20000 ppm of fluoride respectively with the pH varying from acidic values to neutral ones. In this study, the effects of fluoride concentration and pH value on the corrosion behavior of Nb-10Ta-1Re and Ti-6Al-4V alloys in artificial saliva at 37°C were investigated by electrochemical measurements. For both alloys, electrochemical impedance spectroscopy and potentiodynamic polarization results showed that the corrosion rate increased with decreasing pH; also, increasing fluoride concentrations resulted in an increase in the corrosion rate. EIS results suggested that the oxide layer of Ti-6Al-4V alloy became porous in artificial saliva with high fluoride concentrations; on the contrary, Nb-10Ta-1Re alloy retained its compact oxide layer. Scanning electron microscopy results showed that after 5 days of immersion the oxide layer was washed away from the surface of Ti-6Al-4V alloy. For Nb-10Ta-1Re alloy; however, the polishing scratches were evident. At low pH values and high fluoride concentrations Nb-10Ta-1Re alloy showed better corrosion resistance in comparison with Ti-6Al-4V alloy.

Key words: downloadable, Niobium alloys, fluoride, electrochemical impedance, corrosion, dental implant

Dental implants are exposed to a wide range of pH values of saliva and different concentrations of fluoride. In order to prevent plaque and caries formation, prophylactic products have been used more commonly for dental treatments. These products contain different concentrations of fluoride, for example; bucal rinses, toothpastes and gels contain 200ppm, 1000-1500 ppm and 10000-20000 ppm of fluoride respectively with the pH varying from acidic values to neutral ones. In this study, the effects of fluoride concentration and pH value on the corrosion behavior of Nb-10Ta-1Re and Ti-6Al-4V alloys in artificial saliva at 37°C were investigated by electrochemical measurements. For both alloys, electrochemical impedance spectroscopy and potentiodynamic polarization results showed that the corrosion rate increased with decreasing pH; also, increasing fluoride concentrations resulted in an increase in the corrosion rate. EIS results suggested that the oxide layer of Ti-6Al-4V alloy became porous in artificial saliva with high fluoride concentrations; on the contrary, Nb-10Ta-1Re alloy retained its compact oxide layer. Scanning electron microscopy results showed that after 5 days of immersion the oxide layer was washed away from the surface of Ti-6Al-4V alloy. For Nb-10Ta-1Re alloy; however, the polishing scratches were evident. At low pH values and high fluoride concentrations Nb-10Ta-1Re alloy showed better corrosion resistance in comparison with Ti-6Al-4V alloy.

Key words: downloadable, Niobium alloys, fluoride, electrochemical impedance, corrosion, dental implant

Product tags
Also Purchased
Picture for Electrochemical Corrosion Behavior of Niobium Alloys as Metallic Bio-Implants
Available for download

51316-7270-Electrochemical Corrosion Behavior of Niobium Alloys as Metallic Bio-Implants

Product Number: 51316-7270-SG
ISBN: 7270 2016 CP
Author: Wei Wang
Publication Date: 2016
$20.00

Mechanical properties and microstructure of Nb-Ta-Re, Nb-Re, Nb-Pd, and Nb-Pt alloys were studied by nano-indentation measurements and X-ray diffraction. Corrosion behavior was compared by electrochemical methods, including open circuit potential measurement, potentiodynamic, and electrochemical impedance spectroscopy.
Picture for Impact of Microstructure on Hydrogen Solubility and Diffusivity in UNS 07718
Available for download

51316-7267-Impact of Microstructure on Hydrogen Solubility and Diffusivity in UNS 07718

Product Number: 51316-7267-SG
ISBN: 7267 2016 CP
Author: Olesya Golenishcheva, Georg Andersohn, Matthias Oechsner, Jutta Kloewer
Publication Date: 2016
$20.00

To investigate the role of Cr and Cu in steels in different solutions, four kinds of low carbon steel with different Cr and Cu concentrations were prepared to investigate the effect of alloying elements on their corrosion behavior. Solutions of 3.5 wt.% NaCl, diluted hydrochloric acid and diluted sulphuric acid (pH=1.4-1.5) were used.
Picture for Monitoring of Corrosion Rate and Evaluation of Deposited Sea Salt Distributed inside Steel Pipe for
Available for download

51316-7266-Monitoring of Corrosion Rate and Evaluation of Deposited Sea Salt Distributed inside Steel Pipe for Transmission Tower Located at Coastal Environment

Product Number: 51316-7266-SG
ISBN: 7266 2016 CP
Author: Atsushi Naganuma
Publication Date: 2016
$20.00
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support