51313-02130-Electrochemical and SCC Inhibition of Multi-Alloy Systems Using Vapor Corrosion Inhibitors

Product Number: 51313-02130-SG
ISBN: 02130 2013 CP
Author: Behzad Bavarian
Publication Date: 2013
$0.00
$20.00
$20.00

Commercially available inhibitors were successfully investigated for their effectiveness in reducing the corrosion susceptibility of the turbo expander and steam/gas turbine industry alloys. However due to the fact that the power generating system is complex and consists of a multi-alloy system the investigation was expanded to study the corrosion behavior and stress corrosion susceptibility of other alloys such as copper brass (C36600 (38% Zn) Eco-brass (21% Zn) and red brass (8% Zn) nickel plated-copper and titanium alloys (grade 5 and grade 23) in the presence of these inhibitors. Electrochemical behavior (cyclic polarization and EIS) of these alloys in a 200 ppm Cl- solutions + different percentages of inhibitor showed significant improvement in passivity breakdown potentials and their critical pitting temperature. The data acquired from EIS tests showed that inhibitor adsorption to the alloy surfaces fits with the Langmuir adsorption isotherm; the enthalpy of adsorption is about -10 to -16 kJ/mol suggesting that this chemical compound provides physisorption to the surfaces of these alloys. No susceptibility to environmentally-assisted cracking using ASTM G44 and G38 standards was observed.
 

Commercially available inhibitors were successfully investigated for their effectiveness in reducing the corrosion susceptibility of the turbo expander and steam/gas turbine industry alloys. However due to the fact that the power generating system is complex and consists of a multi-alloy system the investigation was expanded to study the corrosion behavior and stress corrosion susceptibility of other alloys such as copper brass (C36600 (38% Zn) Eco-brass (21% Zn) and red brass (8% Zn) nickel plated-copper and titanium alloys (grade 5 and grade 23) in the presence of these inhibitors. Electrochemical behavior (cyclic polarization and EIS) of these alloys in a 200 ppm Cl- solutions + different percentages of inhibitor showed significant improvement in passivity breakdown potentials and their critical pitting temperature. The data acquired from EIS tests showed that inhibitor adsorption to the alloy surfaces fits with the Langmuir adsorption isotherm; the enthalpy of adsorption is about -10 to -16 kJ/mol suggesting that this chemical compound provides physisorption to the surfaces of these alloys. No susceptibility to environmentally-assisted cracking using ASTM G44 and G38 standards was observed.
 

Product tags
Also Purchased
Picture for Weld Seam Corrosion of Steel Sprinkler Pipe
Available for download

51313-02140-Weld Seam Corrosion of Steel Sprinkler Pipe

Product Number: 51313-02140-SG
ISBN: 02140 2013 CP
Author: Paul Su
Publication Date: 2013
$20.00
Picture for CP of Offshore Jacket by Remote Anode Sleds and Discussion About Current Drain to Buried Structures
Available for download

51313-02121-CP of Offshore Jacket by Remote Anode Sleds and Discussion About Current Drain to Buried Structures

Product Number: 51313-02121-SG
ISBN: 02121 2013 CP
Author: Svenn Magne Wigen
Publication Date: 2013
$20.00
Picture for The Impact of Corrosion on Mine Water Supply Systems
Available for download

51313-02137-The Impact of Corrosion on Mine Water Supply Systems

Product Number: 51313-02137-SG
ISBN: 02137 2013 CP
Author: Zoe Coull
Publication Date: 2013
$20.00