51316-7231-Effect of Surface Finishes on the Atmospheric Corrosion of Duplex Grade UNS S32205: Results of a Field Exposure Program in Dubai

Picture for Effect of Surface Finishes on the Atmospheric Corrosion of Duplex Grade UNS S32205: Results of a Fie
Available for download

The main objective with this paper is to present information about the effect of different surface finishes on the corrosion and aesthetic appearance of the duplex grade S32205 exposed at a marine test site in Dubai, UAE. The results obtained include the effect of characteristics such as surface roughness, surface treatment and surface orientation after several years of exposure.

Product Number: 51316-7231-SG
ISBN: 7231 2016 CP
Author: Sukanya Mameng
Publication Date: 2016
$0.00
$20.00
$20.00

 

The duplex grade UNS S32205 is an excellent choice in many marine environments where UNS S31603 is on the borderline in regards to atmospheric corrosion resistance. The properties of S32205 make it well suited for construction with respect to strength, reduced maintenance, durability and long-term service. In marine environments the use of a sufficiently highly alloyed stainless steel, often in combination with a good surface finish and adequate maintenance, is required to maintain pristine surfaces.

The main objective with this paper is to present information about the effect of different surface finishes on the corrosion and aesthetic appearance of the duplex grade S32205 exposed at a marine test site in Dubai, UAE. The results obtained include the effect of characteristics such as surface roughness, surface treatment and surface orientation after several years of exposure. Results show that duplex grade UNS S32205 can be considered for architectural materials in severe marine locations such as the Dubai site. A smooth surface and an appropriate surface treatment give improved corrosion resistance. Chromium and silicon in the passive film were found to be beneficial in terms of resistance to aesthetic degradation. A correlation was observed between aqueous corrosion resistance measured in laboratory pitting corrosion tests and the atmospheric field test results.

 

 

Key word: Downloadable, duplex stainless steel, atmospheric corrosion, degradation, surface finish

 

The duplex grade UNS S32205 is an excellent choice in many marine environments where UNS S31603 is on the borderline in regards to atmospheric corrosion resistance. The properties of S32205 make it well suited for construction with respect to strength, reduced maintenance, durability and long-term service. In marine environments the use of a sufficiently highly alloyed stainless steel, often in combination with a good surface finish and adequate maintenance, is required to maintain pristine surfaces.

The main objective with this paper is to present information about the effect of different surface finishes on the corrosion and aesthetic appearance of the duplex grade S32205 exposed at a marine test site in Dubai, UAE. The results obtained include the effect of characteristics such as surface roughness, surface treatment and surface orientation after several years of exposure. Results show that duplex grade UNS S32205 can be considered for architectural materials in severe marine locations such as the Dubai site. A smooth surface and an appropriate surface treatment give improved corrosion resistance. Chromium and silicon in the passive film were found to be beneficial in terms of resistance to aesthetic degradation. A correlation was observed between aqueous corrosion resistance measured in laboratory pitting corrosion tests and the atmospheric field test results.

 

 

Key word: Downloadable, duplex stainless steel, atmospheric corrosion, degradation, surface finish

Product tags
Also Purchased
Picture for Detecting Inhibitor Migration Depth in Topically-Treated Concrete Using DART-MS
Available for download

51316-7235-Detecting Inhibitor Migration Depth in Topically-Treated Concrete Using DART-MS

Product Number: 51316-7235-SG
ISBN: 7235 2016 CP
Author: Ming Shen
Publication Date: 2016
$20.00

Direct Analysis in Real Time Mass Spectrometry (DART-MS) is an ambient atmosphere mass spectrometry technique. Two concrete topical treatments were studied. One is a penetrating silane sealer. The other is a pure migrating inhibitor topical product.
Picture for Eddy Current for Sizing Cracks in Canisters for Dry Storage Casks – Laboratory Measurements
Available for download

51316-7244-Eddy Current for Sizing Cracks in Canisters for Dry Storage Casks – Laboratory Measurements”

Product Number: 51316-7244-SG
ISBN: 7244 2016 CP
Author: Ryan Meyer
Publication Date: 2016
$20.00

This paper will provide an overview of activities related to the nondestructive examination of dry storage casks for spent nuclear fuel.  The aim is to help ensure their integrity over extended interim storage periods.
Picture for Corrosion Risk Assessment and Cathodic Protection for Aging Electric Utility Transmission Sructures
Available for download

51316-7245-Corrosion Risk Assessment and Cathodic Protection for Aging Electric Utility Transmission Sructures

Product Number: 51316-7245-SG
ISBN: 7245 2016 CP
Author: Mehrooz Zamanzadeh
Publication Date: 2016
$20.00

Discussion on Transmission and Distribution (T&D) structures and system-wide cathodic protection as a mitigation technique. In general soil, corrosivity, lack of cathodic protection/coating, stray current AC interference and copper grounding should be considered in design of T&D structures.
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support