Effect Of Salt Concentration On Uniform H2S Corrosion Rate Of Pipeline Steel At 100 Ppm H2S(G) And 20Oc

Effect Of Salt Concentration On Uniform H2S Corrosion Rate Of Pipeline Steel At 100 Ppm H2S(G) And 20Oc
Available for download

Large amounts of water can be produced during extraction of hydrocarbons from underground reservoirs.1 It is well understood that produced waters usually contain high amounts of dissolved salts, up to 28 wt.%.2 In addition to salts, dissolved corrosive gases (CO2 and H2S) are present in produced water, which make the mixture a complex corrosive environment for metallic parts and equipment used throughout the production process. 

Product Number: 51322-17982-SG
Author: Fazlollah Madani Sani, Bruce Brown, Srdjan Nesic
Publication Date: 2022
Industry: Water/Wastewater
$0.00
$20.00
$20.00

Large amounts of water can be produced during the production of hydrocarbons from underground reservoirs. Salts are always dissolved in these produced waters. The concentration of dissolved salts can be as high as 400 g/l. For the first time, the effect of salt concentration on uniform hydrogen sulfide (H2S) corrosion of carbon steel in aqueous solutions is studied. Linear polarization resistance (LPR) and potentiodynamic polarization (PD) experiments were conducted in aqueous solutions at 20oC and pH 5.00 saturated with an H2S/N2 gas mixture with a total pressure of 1 bar and H2S concentration of 100 ppm(v). Two NaCl concentrations were tested: 1 and 20 wt.%. A rotating cylinder electrode with a rotational speed of 1000 rpm was used as the specimen. LPR corrosion rates indicated that H2S corrosion rate decreased with increasing salt concentration. PD results showed that the corrosion process was under mixed control. Increasing salt concentration retarded both the anodic and the cathodic reactions, and thereby, decreased the rate of uniform H2S corrosion. 

Large amounts of water can be produced during the production of hydrocarbons from underground reservoirs. Salts are always dissolved in these produced waters. The concentration of dissolved salts can be as high as 400 g/l. For the first time, the effect of salt concentration on uniform hydrogen sulfide (H2S) corrosion of carbon steel in aqueous solutions is studied. Linear polarization resistance (LPR) and potentiodynamic polarization (PD) experiments were conducted in aqueous solutions at 20oC and pH 5.00 saturated with an H2S/N2 gas mixture with a total pressure of 1 bar and H2S concentration of 100 ppm(v). Two NaCl concentrations were tested: 1 and 20 wt.%. A rotating cylinder electrode with a rotational speed of 1000 rpm was used as the specimen. LPR corrosion rates indicated that H2S corrosion rate decreased with increasing salt concentration. PD results showed that the corrosion process was under mixed control. Increasing salt concentration retarded both the anodic and the cathodic reactions, and thereby, decreased the rate of uniform H2S corrosion. 

Product tags
Also Purchased
Picture for Comparison of corrosion behavior of X65 pipeline steel in CO2-H2S and CO2 environment at different f
Available for download

51312-01238-Comparison of corrosion behavior of X65 pipeline steel in CO2-H2S and CO2 environment at different f

Product Number: 51312-01238-SG
ISBN: 01238 2012 CP
Author: Wei Liu
Publication Date: 2012
$20.00
Picture for Localized Corrosion of Mild Steel under Iron Sulfide Layers in CO2/H2S Environment
Available for download

51318-10990-Localized Corrosion of Mild Steel under Iron Sulfide Layers in CO2/H2S Environment

Product Number: 51318-10990-SG
Author: Saba Navabzadeh Esmaeely / Gheorghe Bota / Bruce Brown / Srdjan Nesic
Publication Date: 2018
$20.00

Mild steel specimens (API 5L X65) were pretreated to form a pyrrhotite layer on the surface using high temperature sulfidation in oil, then exposed to a range of aqueous CO2 and H2S corrosion environments, leading to initiation of localized corrosion.

 
Electrochemical and Morphological Investigation of Corrosion Behavior of C1018 in a Subcritical and Supercritical CO2 Environment with Presence of H2S
Available for download

Electrochemical And Morphological Investigation Of Corrosion Behavior Of Carbon Steel In A Supercritical CO2 Environment With Presence Of H2S.

Product Number: 51322-18005-SG
Author: Yuan Ding, Chin-Hua “Jim” Cheng, Raymundo Case
Publication Date: 2022
$20.00

Supercritical CO2 storage has been gaining more attention due to its wider application. It is one of the desirable solutions for reducing CO2 emission, which is an important contributor to the global climate crisis. In other cases, some of the early applications were focused on the oil and gas industry, by using supercritical CO2 to sequence the mature wells for better production [1],[2]. In those environments, C1018 carbon steel was extensively used, due to its good balance of toughness, strength, and ductility as well as its excellent weldability. 
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support