51318-11107-Effect of Oxygen in Back Shielding Gas on Corrosion Resistance of Super Duplex Stainless Steel Pipe

Picture for Effect of Oxygen in Back Shielding Gas on Corrosion Resistance of Super Duplex Stainless Steel Pipe
Available for download

The effect of back shielding gas types and contained oxygen level on the corrosion resistance of welds was investigated for gas tungsten arc welding (GTAW) of UNS S32750 super duplex stainless steel (SDSS) pipes.

Product Number: 51318-11107-SG
Author: Takayuki Tokumine / Takanori Mimoto / Gen Ogita / Yoshiyuki Shimizu / Masanori Gokou / Fu-Gao Wei / Toshiaki Ashitani / Masayuki Tanaka
Publication Date: 2018
Industry: Materials Selection and Design
$0.00
$20.00
$20.00

The effect of back shielding gas types and contained oxygen level on the corrosion resistance of weld was investigated for gas tungsten arc welding (GTAW) of UNS S32750 super duplex stainless steel (SDSS) pipes. The SDSS pipes were welded with three types of back shielding gases of nominal 100% Ar, 100% N2 and a mixture of 90% N2+10% H2 along with controlled O2 contents at 100, 500 and 2,000 ppm as pre-mixed gas. It was found that 100% N2 back shielding gas improves the corrosion resistance compared to 100% Ar, however, a mixture of 90% N2+10% H2 had an adverse effect. In addition, the specimen employing 100% N2 back shielding gas with 2,000 ppmO2 was acceptable in corrosion test. It was observed that the corrosion resistance of SDSS weld joint is mainly affected by depletion of nitrogen in the surface of root bead and less affected by oxygen content levels. The nitrogen depletion behavior is affected by the type of back shielding gas.

Key words: Super duplex stainless steel, UNS S32750, single-sided welding, GTAW, oxidation, corrosion resistance

The effect of back shielding gas types and contained oxygen level on the corrosion resistance of weld was investigated for gas tungsten arc welding (GTAW) of UNS S32750 super duplex stainless steel (SDSS) pipes. The SDSS pipes were welded with three types of back shielding gases of nominal 100% Ar, 100% N2 and a mixture of 90% N2+10% H2 along with controlled O2 contents at 100, 500 and 2,000 ppm as pre-mixed gas. It was found that 100% N2 back shielding gas improves the corrosion resistance compared to 100% Ar, however, a mixture of 90% N2+10% H2 had an adverse effect. In addition, the specimen employing 100% N2 back shielding gas with 2,000 ppmO2 was acceptable in corrosion test. It was observed that the corrosion resistance of SDSS weld joint is mainly affected by depletion of nitrogen in the surface of root bead and less affected by oxygen content levels. The nitrogen depletion behavior is affected by the type of back shielding gas.

Key words: Super duplex stainless steel, UNS S32750, single-sided welding, GTAW, oxidation, corrosion resistance

Product tags
Also Purchased
Picture for Effects of nitride precipitation in duplex stainless steel
Available for download

51318-10512-Effects of nitride precipitation in duplex stainless steel

Product Number: 51318-10512-SG
Author: Marco De Marco / Marco Palombo / Anthony Pianezze / Abderrahmane Taiche / Valentina Spinelli / Marina Delucchi
Publication Date: 2018
$20.00

The aim of this paper is to find a correlation between nitride content/distribution and properties of two of the largely adopted Duplex Stainless Steel (DSS), UNS* S32205 and UNS S32750. *Unified Numbering System
Picture for Influence of tungsten on passivity breakdown and repassivation of 25Cr super duplex stainless steels
Available for download

51318-11102-Influence of tungsten on passivity breakdown and repassivation of 25Cr super duplex stainless steels

Product Number: 51318-11102-SG
Author: Cristian Torres / Mariano Kappes / Roy Johnsen / Mariano Iannuzzi
Publication Date: 2018
$20.00

Two super duplex stainless steels were investigated: a W-free (UNS S32750) and a 2.1 wt% W-containing (UNS S39274) grade. Goals: To study localized corrosion resistance of super duplex stainless steels and how W affects the same.
Picture for 11255 Pitting Corrosion Mechanisms of Lean Duplex
Available for download

11255 Pitting Corrosion Mechanisms of Lean Duplex, Duplex and Super Duplex Stainless Steels in Chloride Solutions

Product Number: 51300-11255-SG
ISBN: 2011 11255 CP
Author: J. Saithala, J. Atkinson, H Ubhi, A. Patil
Publication Date: 2011
$20.00
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support