Effect of Blocking Compound on Electrochemical Corrosion Behavior of Wire Rope at Gulf of Mexico Surface and Subsea Temperatures

Wire ropes with a sheathed spiral strand are commonly used for mooring applications in offshore oil and gas production. Each strand comprises a bundle of galvanized steel wires with a blocking compound applied to the outer layer of the wire bundle to prevent seawater from contacting the internal strands of wire if there is a breach in the urethane cover. The blocking compound and a sacrificial zinc layer on each strand of wire are designed to protect the carbon steel.  

Depending on the water depth where the wire rope is being used offshore, it can experience a wide range of temperatures—from 22°C at the surface to 4°C at the seabed. Corrosion behavior of wires at these temperatures is critical, in case of breach in the urethane cover. 

Immersion and electrochemical corrosion testing was performed on subsea mooring line wire rope with and without blocking compound in synthetic seawater at 4°C, 13°C, and 22°C. Samples of galvanized wire with and without blocking compound at the lowest temperature (4°C) did not exhibit any iron corrosion products even after 160 days of exposure to synthetic seawater. The corrosion rate of galvanized steel with blocking compound remained less than 2 mpy, while that for galvanized steel without blocking compound remained less than 5 mpy. 

Product Number: 51320-14262-SG
Author: Suresh Divi, Swight Janoff
Publication Date: 2020
$0.00
$20.00
$20.00
Also Purchased
Picture for Wire/Strand Slippage in Anchorages—A Potential Failure Mode for Corroding Post-Tensioning Tendons
Available for download

51315-5461-Wire/Strand Slippage in Anchorages—A Potential Failure Mode for Corroding Post-Tensioning Tendons

Product Number: 51315-5461-SG
ISBN: 5461 2015 CP
Author: William Hartt
Publication Date: 2015
$20.00
Picture for Corrosion Fatigue Behaviour of High Strength Steel Wire in Various Aqueous Environments
Available for download

51315-5605-Corrosion Fatigue Behaviour of High Strength Steel Wire in Various Aqueous Environments

Product Number: 51315-5605-SG
ISBN: 5605 2015 CP
Author: Peter Barnes
Publication Date: 2015
$0.00
Picture for 98498 LARGE DIAMETER WIRE, HIGH DEPOSITION
Available for download

98498 LARGE DIAMETER WIRE, HIGH DEPOSITION METALIZING: A COMPETITIVE EDGE FOR LONG LIFE COATINGS

Product Number: 51300-98498-SG
ISBN: 98498 1998 CP
Author: Mahlon S. Wixon
$20.00