51317--9780-Development of Test Methods and Factors for Evaluation of Oilfield Corrosion Inhibitors at High Temp

Picture for Development of Test Methods and Factors for Evaluation of Oilfield Corrosion Inhibitors at High Temp
Picture for Development of Test Methods and Factors for Evaluation of Oilfield Corrosion Inhibitors at High Temp Picture for Development of Test Methods and Factors for Evaluation of Oilfield Corrosion Inhibitors at High Temp
Available for download

Evaluation of corrosion inhibitors for high temperature (HT) upstream oilfield applications can be challenging. A series of laboratory testing methodologies were conducted to further elucidate the factors which affect laboratory corrosion inhibitor performance in high temperature conditions.

Product Number: 51317--9780-SG
ISBN: 9780 2017 CP
Author: Boyd Laurent
Publication Date: 2017
Industry: Chemical Inhibitors
$0.00
$20.00
$20.00

Evaluation of corrosion inhibitors for high temperature (HT) upstream oilfield applications can be challenging due to fixed fluid volume tests typically encountered in laboratory testing. A series of laboratory testing methodologies were conducted in order to further elucidate the factors which affect laboratory corrosion inhibitor performance in high temperature conditions. Under certain HT conditions inhibitor performance may be skewed due to testing effects which may occur in closed cell testing at HT such as Fe2+ saturation and/or scaling of the test fluids which may artificially lower the overall general corrosion rate. This testing program was designed to minimize these effects and ensure that corrosion inhibition in laboratory testing is identified solely due to performance of the inhibitor. For these studies corrosion measurements in stirred autoclaves were performed by linear polarization resistance (LPR) or with weight loss measurements in rotating cage autoclaves (RCA). Surface morphology of corrosion products scale deposition and effects of localized attack were evaluated by microscopic evaluations. Factors affecting inhibited and uninhibited general corrosion rates measured in laboratory test environments such as brine composition effect of scale inhibitor inclusion effect of metal surface area to fluid volume ratio and method of acid gas charging were evaluated.

Key words: High Temperature, Corrosion Testing, Corrosion Inhibitor Selection

 

Evaluation of corrosion inhibitors for high temperature (HT) upstream oilfield applications can be challenging due to fixed fluid volume tests typically encountered in laboratory testing. A series of laboratory testing methodologies were conducted in order to further elucidate the factors which affect laboratory corrosion inhibitor performance in high temperature conditions. Under certain HT conditions inhibitor performance may be skewed due to testing effects which may occur in closed cell testing at HT such as Fe2+ saturation and/or scaling of the test fluids which may artificially lower the overall general corrosion rate. This testing program was designed to minimize these effects and ensure that corrosion inhibition in laboratory testing is identified solely due to performance of the inhibitor. For these studies corrosion measurements in stirred autoclaves were performed by linear polarization resistance (LPR) or with weight loss measurements in rotating cage autoclaves (RCA). Surface morphology of corrosion products scale deposition and effects of localized attack were evaluated by microscopic evaluations. Factors affecting inhibited and uninhibited general corrosion rates measured in laboratory test environments such as brine composition effect of scale inhibitor inclusion effect of metal surface area to fluid volume ratio and method of acid gas charging were evaluated.

Key words: High Temperature, Corrosion Testing, Corrosion Inhibitor Selection

 

Product tags
Also Purchased
Picture for Development of Application Friendly Products for Wet Gas Corrosion Inhibition
Available for download

51317--9519-Development of Application Friendly Products for Wet Gas Corrosion Inhibition

Product Number: 51317--9519-SG
ISBN: 9519 2017 CP
Author: Jeffery Clark
Publication Date: 2017
$20.00

An operator in North America discovered an internal corrosion failure in a wet gas system directly below the point of injection of a water-soluble corrosion inhibitor (CI). Tests using low shear rotating cage autoclaves and a dual autoclave system were performed as a corrosion screening method.
Picture for 02288 EVALUATION OF INHIBITOR PERFORMANCE...
Available for download

02288 EVALUATION OF INHIBITOR PERFORMANCE FOR PROTECTION AGAINST LOCALIZED CORROSION

Product Number: 51300-02288-SG
ISBN: 02288 2002 CP
Author: J. Marsh, J. W. Palmer and R. C. Newman
Publication Date: 2002
$20.00

 A novel evaluation technique, based on an artificial pit electrode, has been developed for inhibitor studies. The first example is of three generic inhibitors, against localised corrosion. The second is of three industrial inhibitors against existing localised corrosion on a north sea production platform
Picture for Standards for Laboratory Evaluation of Corrosion Inhibitors
Available for download

51314-3980-Standards for Laboratory Evaluation of Corrosion Inhibitors

Product Number: 51314-3980-SG
ISBN: 3980 2014 CP
Author: Sankara Papavinasam
Publication Date: 2014
$20.00
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support