Corrosion Behavior Of UNS S31600 In Purified Molten Salts

Product Number: 51321-16945-SG
Author: Chi Ying Loh; Jared O. Butner; Connor J. Veronese; Christopher J. Faraj; Chi Ying Loh; Jared O. Butner; Connor J. Veronese; Christopher J. Faraj; Vilupanur A. Raviilupanur A. Ravi
Publication Date: 2021
$0.00
$20.00
$20.00

Chloride salt mixtures have been proposed as candidates to improve the efficiency of CSP plants, due to their high thermal stability, thermal conductivity, heat capacity and low cost. However, molten chlorides are highly corrosive, and impurities in salts like magnesium chloride can increase the corrosivity of this salt mixture. Therefore, an in situ method of purifying the mixture was applied to mitigate the severity of their corrosive effects on the containment materials. The molten salt corrosion behavior of UNS S31600 at 700°C was evaluated in (a) the purified KCl-20 mol% NaCl- 20 mol% MgCl2 salt mixture and (b) in mixtures using as-received salts. Electrochemical tests were performed according to the ASTM G59-97 standard to determine the corrosion behavior of metallic alloy pre- and post- salt purification.

Chloride salt mixtures have been proposed as candidates to improve the efficiency of CSP plants, due to their high thermal stability, thermal conductivity, heat capacity and low cost. However, molten chlorides are highly corrosive, and impurities in salts like magnesium chloride can increase the corrosivity of this salt mixture. Therefore, an in situ method of purifying the mixture was applied to mitigate the severity of their corrosive effects on the containment materials. The molten salt corrosion behavior of UNS S31600 at 700°C was evaluated in (a) the purified KCl-20 mol% NaCl- 20 mol% MgCl2 salt mixture and (b) in mixtures using as-received salts. Electrochemical tests were performed according to the ASTM G59-97 standard to determine the corrosion behavior of metallic alloy pre- and post- salt purification.

Also Purchased
Picture for Hot Corrosion of Nickel-Chromium Alloys in a Molten Eutectic Salt Environment
Available for download

51316-7824-Hot Corrosion of Nickel-Chromium Alloys in a Molten Eutectic Salt Environment

Product Number: 51316-7824-SG
ISBN: 7824 2016 CP
Author: Vilupanur Ravi
Publication Date: 2016
$20.00
Picture for Electrochemical Characterization of High Alloyed Materials in Molten Salts for Solar Energy Applicat
Available for download

51315-5659-Electrochemical Characterization of High Alloyed Materials in Molten Salts for Solar Energy Applications

Product Number: 51315-5659-SG
ISBN: 5659 2015 CP
Author: Ralph Baessler
Publication Date: 2015
$20.00
Picture for Effect of Chloride Content on The Corrosion Behavior of Ferritic and Austenitic Steels in Molten Sol
Available for download

51316-7494-Effect of Chloride Content on The Corrosion Behavior of Ferritic and Austenitic Steels in Molten Solar Salts

Product Number: 51316-7494-SG
ISBN: 7494 2016 CP
Author: Ali Soleimani Dorcheh
Publication Date: 2016
$20.00