Characterization of Accelerated Test Environments Using Galvanically Coupled Multi-Electrode Arrays

Product Number: 51315-5982-SG
ISBN: 5982 2015 CP
Author: Erica Macha
Publication Date: 2015
$0.00
$0.00
$0.00

The difficulty of replicating service-environment corrosion failure modes in accelerated laboratory testing is a well-known and well-documented challenge facing the atmospheric corrosion community. Several recent studies have highlighted the importance of cyclic variations in the test environment in recreating corrosion damage which is similar to real-world damage. A thorough understanding of the effects of these cyclic variations is critical to the development of improved accelerated tests. In this work multi-electrode arrays and corrosion sensors are used to characterize the corrosion susceptibility of metals and galvanic couples exposed to several common accelerated tests. A multi-electrode array composed of steel in an aluminum matrix is used to simulate a steel fastener in a Al 2024 panel. Spatial distributions of current are examined as a function of test environment and cycle. Using creviced sensors and multi–electrode arrays the effects of cycling humidity and temperature on crevice environments are also examined.

The difficulty of replicating service-environment corrosion failure modes in accelerated laboratory testing is a well-known and well-documented challenge facing the atmospheric corrosion community. Several recent studies have highlighted the importance of cyclic variations in the test environment in recreating corrosion damage which is similar to real-world damage. A thorough understanding of the effects of these cyclic variations is critical to the development of improved accelerated tests. In this work multi-electrode arrays and corrosion sensors are used to characterize the corrosion susceptibility of metals and galvanic couples exposed to several common accelerated tests. A multi-electrode array composed of steel in an aluminum matrix is used to simulate a steel fastener in a Al 2024 panel. Spatial distributions of current are examined as a function of test environment and cycle. Using creviced sensors and multi–electrode arrays the effects of cycling humidity and temperature on crevice environments are also examined.

Product tags
Also Purchased
Picture for Comprehensive Approach to Oxygen Corrosion Analysis of Water Injection Systems
Available for download

Comprehensive Approach to Oxygen Corrosion Analysis of Water Injection Systems

Product Number: 51315-5962-SG
ISBN: 5962 2015 CP
Author: Troy Eggum
Publication Date: 2015
$0.00
Picture for Application of Non-Intrusive Fixed Wireless Thickness Monitoring for Sulfidation Corrosion to Provi
Available for download
Picture for 241-AY-102 Leak Detection Pit Drain Line Inspection Report
Available for download

51315-6198-241-AY-102 Leak Detection Pit Drain Line Inspection Report

Product Number: 51315-6198-SG
ISBN: 6198 2015 CP
Author: Brandon Vazquez
Publication Date: 2015
$0.00