97356 STRESS CORROSION OF FIBERGLASS-REINFORCED (FRP) COMPOSITES

Product Number: 51300-97356-SG
ISBN: 97356 1997 CP
Author: S.J. Youd, D.H. Kelley, S.N. Sapalidis, P.J. Hogg
$0.00
$20.00
$20.00
The stress conosion characteristics of uniaxial glass tibre reinforced thermosetting resin composites have been examined in Hydrochloric acid at room temperature and 80 °C. A simple technique based on linear elastic fracture mechanics (LEFM) is presented for characterizing crack growth in these materials subjected to hostile acidic environments The enviromnental stress corrosion cracking is investigated both for different types of resin and different types of glass tibre reinforcements. Two matrices were used : Bis-A epoxy vinyl ester resin (based on Bisphenol-A epoxy resin) and novolac epoxy vinyl ester resin (based on epoxidised novolac resin). Two glass tibre types were employed : standard E-glass fibre and “R’, a special type of E-glass with superior acid resistance. Model experiments using a modified double cantilever beam test with static loading have been carried out on unidirectional composite specimens in 1M Hydrochloric acid solution at room temperature and 80 °C. The rate of crack growth in the specimen depends on the applied stress, the temperature and the environment. Consequently, the Iifetime of a component or strocture made from GRP, subjected to stress corrosion conditions, could be predicted provided the dependence of crack growth rate on stress intensity at the crack tip is known. Scanning electron microscopy studies of the specimen fracture surfaces have identified the characteristic failure mechanisms. The most important findings of this work is that the selection of epoxy vinyl ester resins reinforced with “R” fibre exhibited superior resistance to crack growth at 80 °C compared to similar E-glass reinforced composites at room temperatures. Keywords: composite materials, FRP, GRP, glass fibres, epoxy resin, vinylester resin, acidic conditions, hydrochloric acid, cracking, stress corrosion, crack growth
The stress conosion characteristics of uniaxial glass tibre reinforced thermosetting resin composites have been examined in Hydrochloric acid at room temperature and 80 °C. A simple technique based on linear elastic fracture mechanics (LEFM) is presented for characterizing crack growth in these materials subjected to hostile acidic environments The enviromnental stress corrosion cracking is investigated both for different types of resin and different types of glass tibre reinforcements. Two matrices were used : Bis-A epoxy vinyl ester resin (based on Bisphenol-A epoxy resin) and novolac epoxy vinyl ester resin (based on epoxidised novolac resin). Two glass tibre types were employed : standard E-glass fibre and “R’, a special type of E-glass with superior acid resistance. Model experiments using a modified double cantilever beam test with static loading have been carried out on unidirectional composite specimens in 1M Hydrochloric acid solution at room temperature and 80 °C. The rate of crack growth in the specimen depends on the applied stress, the temperature and the environment. Consequently, the Iifetime of a component or strocture made from GRP, subjected to stress corrosion conditions, could be predicted provided the dependence of crack growth rate on stress intensity at the crack tip is known. Scanning electron microscopy studies of the specimen fracture surfaces have identified the characteristic failure mechanisms. The most important findings of this work is that the selection of epoxy vinyl ester resins reinforced with “R” fibre exhibited superior resistance to crack growth at 80 °C compared to similar E-glass reinforced composites at room temperatures. Keywords: composite materials, FRP, GRP, glass fibres, epoxy resin, vinylester resin, acidic conditions, hydrochloric acid, cracking, stress corrosion, crack growth
PRICE BREAKS - The more you buy, the more you save
Quantity
1+
5+
Price
$20.00
$20.00
Product tags
Also Purchased
Picture for 97349 A RECOMMENDED FRP INSPECTION PROCEDURE
Available for download

97349 A RECOMMENDED FRP INSPECTION PROCEDURE FOR THE END-USER

Product Number: 51300-97349-SG
ISBN: 97349 1997 CP
Author: Terry W. Cowley
$20.00
Picture for 98452 MODIFICATION OR REPAIR OF FIBERGLASS
Available for download

98452 MODIFICATION OR REPAIR OF FIBERGLASS REINFORCED PLASTIC (FRP) STRUCTURES

Product Number: 51300-98452-SG
ISBN: 98452 1998 CP
Author: J.G. Johnson, Jr., S. Bigante, W.H. Julius
$20.00
Picture for 97351 FRP EQUIPMENT: DO YOU KNOW
Available for download

97351 FRP EQUIPMENT: DO YOU KNOW WHAT YOU ARE BUYING?

Product Number: 51300-97351-SG
ISBN: 97351 1997 CP
Author: Robert C. Hawkins
$20.00