97117 EFFECTS OF ETA, PH CHANGE, AND INCREASED HYDRAZINE LEVELS ON DEPOSIT-COVERED ALLOY 600 AND BRASS CORROSION AT INDIAN POINT 2

Picture for 97117 EFFECTS OF ETA, PH CHANGE, AND INCREASED
Available for download
Product Number: 51300-97117-SG
ISBN: 97117 1997 CP
Author: Aaron Barkatt, Ewa Labuda, Donna M. Wilder, Susan Smialowska, Raul B. Rebak, Gahna Cherepakhov, Reyn
$0.00
$20.00
$20.00
Chemical dissolution tests and electrochemical tests were carried out on Alloy 600 specimens covered with synthetic deposit simulating the tube deposits in the steam generators at IndIao Point 2. The tests showed that the introduction of ETA and a moderate increase in pH gave rise to lower corrosion rates, but enhancement of hydrazine levels caused them to rise. In the case of brass, both types of tests showed that raisiig the pH caused the corrosion rates to increase, but the introduction of ETA led to mild decrease in these rates.
Chemical dissolution tests and electrochemical tests were carried out on Alloy 600 specimens covered with synthetic deposit simulating the tube deposits in the steam generators at IndIao Point 2. The tests showed that the introduction of ETA and a moderate increase in pH gave rise to lower corrosion rates, but enhancement of hydrazine levels caused them to rise. In the case of brass, both types of tests showed that raisiig the pH caused the corrosion rates to increase, but the introduction of ETA led to mild decrease in these rates.
PRICE BREAKS - The more you buy, the more you save
Quantity
1+
5+
Price
$20.00
$20.00
Product tags
Also Purchased
Picture for Failures of Brass Components in Water and Steam Systems
Available for download

Failures of Brass Components in Water and Steam Systems

Product Number: 51317--9123-SG
ISBN: 9123 2017 CP
Author: James Dillon
Publication Date: 2017
$20.00

Case histories will illustrate failures that occurred in components that were made of different brass alloys in water and steam systems. Recommendations will be made to mitigate the damage that occurred in each case.
Picture for 51318-11098- Microbial Assisted Cracking of Admiralty Brass Tubes from Lube Oil Cooler
Available for download

51318-11098- Microbial Assisted Cracking of Admiralty Brass Tubes from Lube Oil Cooler

Product Number: 51318-11098-SG
Author: Yousif Al Rabie / Khalid Al-Nabulsi / Faisal Al-Abbas
Publication Date: 2018
$20.00

This work investigates unexpected leaks observed on several cracked admiralty brass tubes that failed after 7 years in operation. Both metallurgical and molecular microbiological methods were used to understand the root cause of these failures.
Picture for The Effect of Shot Peening on Steam Oxidation of Stainless Steel at 600°-650°C
Available for download

The Effect of Shot Peening on Steam Oxidation of Stainless Steel at 600°-650°C

Product Number: 51317--9426-SG
ISBN: 9426 2017 CP
Author: Bruce Pint
Publication Date: 2017
$20.00

This study exposed sections from two commercially shot peened S30409 tubes in 1 bar steam for up to 15,000 h at 600°, 625° and 650°C and specimens were removed at increments to characterize the oxide thickness and microstructure.
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support