97029 PERFORMANCE OF 12CR-4NI IN SIMULATED MODERATELY SOUR PRODUCTION ENVIRONMENTS

Product Number: 51300-97029-SG
ISBN: 97029 1997 CP
Author: RD. Kane, G. Farqrdrar,Dave Sanders
$0.00
$20.00
$20.00
This study indicated that centrifugally cast 12Cr-4Ni material exhibited hardness values up to HRC 40 in the weld metal in the as-welded condition. Upon post weld heat treatment (PWHT), hardness decreased for all locations with maximum values of HRC 26.5 max. in the weld metal. This was above the HRC 23 max. guidelines for sour service indicated by NACE MR0175 for 12Cr-4Ni materials. Slow strain rate (SSR) teats indicated maximum susceptibility to cracking in the condensed brine (1000 ppm chloride) with hydrogen sulfide at 24 C and only very limited cracking susceptibility in the mixed brine with hydrogen tide at 167 C. Autoclave tests conducted in these environments using stressed beam specimens showed susceptibility to SSC at 24 C in base metal, heat affected zone (HAZ) and weld metal. Maximum susceptibility was in the weld metal producing complete failure in both as-welded and PWHT specimens. The base metal specimens showed lower but still significant susceptibility to SSC. At 167 C, none of the 12Cr-4Ni beam specimens failed showing substantial resistance to SCC.
This study indicated that centrifugally cast 12Cr-4Ni material exhibited hardness values up to HRC 40 in the weld metal in the as-welded condition. Upon post weld heat treatment (PWHT), hardness decreased for all locations with maximum values of HRC 26.5 max. in the weld metal. This was above the HRC 23 max. guidelines for sour service indicated by NACE MR0175 for 12Cr-4Ni materials. Slow strain rate (SSR) teats indicated maximum susceptibility to cracking in the condensed brine (1000 ppm chloride) with hydrogen sulfide at 24 C and only very limited cracking susceptibility in the mixed brine with hydrogen tide at 167 C. Autoclave tests conducted in these environments using stressed beam specimens showed susceptibility to SSC at 24 C in base metal, heat affected zone (HAZ) and weld metal. Maximum susceptibility was in the weld metal producing complete failure in both as-welded and PWHT specimens. The base metal specimens showed lower but still significant susceptibility to SSC. At 167 C, none of the 12Cr-4Ni beam specimens failed showing substantial resistance to SCC.
PRICE BREAKS - The more you buy, the more you save
Quantity
1+
5+
Price
$20.00
$20.00
Product tags
Also Purchased
Picture for 97053 THE EFFECT OF LOAD FLUCTUATION ON
Available for download

97053 THE EFFECT OF LOAD FLUCTUATION ON SULPHIDE STRESS CORROSION CRACKING IN C-Mn STEEL WELD METAL

Product Number: 51300-97053-SG
ISBN: 97053 1997 CP
Author: A.C. Elbro, T.G. Gooch, R.J. Pargeter
$20.00
Picture for 97019 MARTENSITIC STAINLESS STEEL SEAMLESS
Available for download

97019 MARTENSITIC STAINLESS STEEL SEAMLESS LINEPIPE WITH SUPERIOR WELDABILITY AND CO2 CORROSION RESISTANCE

Product Number: 51300-97019-SG
ISBN: 97019 1997 CP
Author: Y. Miyata, M. Kimura, T. Koseki, T. Toyooka, F. Murase
$20.00
Picture for 97028 CORROSION PERFORMANCES OF MODIFIED
Available for download

97028 CORROSION PERFORMANCES OF MODIFIED 13Cr FOR OCTG IN OIL AND GAS ENVIRONMENTS

Product Number: 51300-97028-SG
ISBN: 97028 1997 CP
Author: B.J. ORLANS-JOLIET, C.P. LINNE, F. BLANCHARD, G.C. GUNTZ
$20.00