TIIe effects of heat treatment and catholically hydrogen charging on susceptibility of nickel-based superalloy 718 to stress corrosion cracking were studied. Two conditions of solution-annealed (SA) and heat-treated (HT) materials were considered. Slow strain rate tensile tests with strain rates of...
Keywords: alloy 718, stress corrosion cracking, hydrogen embrittlement, cathodic potential