51317-9478-Long-Term Oxidation Performance of High-Temperature Alloys in the Presence of Water Vapor

Evaluation of sheet and foil samples of two Cr2O3- and two Al2O3-forming alloys - tested for 360 days in air + 10 vol. % H2O at 760oC and 871oC. Alloys were ranked on weight change behavior and metal recession measurements, average internal penetration, and maximum internal penetration.

Product Number: 51317-9478-SG
ISBN: 9478 2017 CP
Author: Joseph Meyer / Vinay Deodeshmukh
Publication Date: 2017
$20.00
$20.00
$20.00

High-temperature alloys are susceptible to accelerated oxidation attack in the presence of water vapor, which can affect a components effective lifetime. The overall oxidation performance of the Cr2O3-forming alloys is critically linked to the chromium reservoir as Cr2O3-based scales are prone to vaporization when exposed to water vapor containing environments. This paper evaluates sheet and foil samples of two Cr2O3- and two Al2O3-forming alloys, which were tested for 360 days in air + 10 vol. % H2O at 760oC and 871oC. The alloys were ranked based on weight change behavior as well as metal recession measurements, which includes metal loss, average internal penetration, and maximum internal penetration. The results showed that the Ni-base, Cr2O3-scale forming alloy N06230 was more resistant than Fe-base N08120. An increased oxidation attack among the Cr2O3-formers was observed in sheet samples compared to foil samples. Both Al2O3-scale forming alloys outperformed the Cr2O3-forming alloys due to their ability to form and maintain a thin, adherent, and continuous Al2O3 scale for extended durations.

 

Key words: conference papers, 2017 conference papers, water vapor, oxidation, chromia- and alumina-forming alloys

High-temperature alloys are susceptible to accelerated oxidation attack in the presence of water vapor, which can affect a components effective lifetime. The overall oxidation performance of the Cr2O3-forming alloys is critically linked to the chromium reservoir as Cr2O3-based scales are prone to vaporization when exposed to water vapor containing environments. This paper evaluates sheet and foil samples of two Cr2O3- and two Al2O3-forming alloys, which were tested for 360 days in air + 10 vol. % H2O at 760oC and 871oC. The alloys were ranked based on weight change behavior as well as metal recession measurements, which includes metal loss, average internal penetration, and maximum internal penetration. The results showed that the Ni-base, Cr2O3-scale forming alloy N06230 was more resistant than Fe-base N08120. An increased oxidation attack among the Cr2O3-formers was observed in sheet samples compared to foil samples. Both Al2O3-scale forming alloys outperformed the Cr2O3-forming alloys due to their ability to form and maintain a thin, adherent, and continuous Al2O3 scale for extended durations.

 

Key words: conference papers, 2017 conference papers, water vapor, oxidation, chromia- and alumina-forming alloys

Also Purchased
Picture for 02213 THE INFLUENCE OF ENVIRONMENTAL FACTORS...
Available for download

02213 THE INFLUENCE OF ENVIRONMENTAL FACTORS ON THE CREVICE CORROSION OF ALLOY 625 IN NATURAL SEAWATER

Product Number: 51300-02213-SG
ISBN: 02213 2002 CP
Author: F. J. Martin, P. M. Natishan, K. E. Lucas, E. A. Hogan, A. M. Grolleau, and E. D. Thomas
$20.00
Picture for 01157 APPLICATION OF RHENIUM COATING AS A
Available for download

01157 APPLICATION OF RHENIUM COATING AS A DIFFUSION BARRIER TO IMPROVE THE HIGH TEMPERATURE OXIDATION RESISTANCE OF NICKEL-BASED SUPERALLOY

Product Number: 51300-01157-SG
ISBN: 01157 2001 CP
Author: Toshio Narita, Shigenari Hayashi, Mayumi Shoji, Yoshitake Hisamatsu, Daisuke Yoshida and Michihisa F
$20.00
Picture for 00517 OBSERVATIONS OF THE EFFECT OF WATER VAPOR
Available for download

00517 OBSERVATIONS OF THE EFFECT OF WATER VAPOR ON THE ELEVATED TEMPERATURE OXIDATION OF AUSTENITIC STAINLESS STEEL FOIL

Product Number: 51300-00517-SG
ISBN: 00517 2000 CP
Author: J.M. Rakowski, B.A. Pint
$20.00