11378 Water Effect on Steel Under Supercritical CO2 Condition

Picture for 11378 Water Effect on Steel Under Supercritical CO2 Condition
Available for download
Product Number: 51300-11378-SG
ISBN: 11378 2011 CP
Author: Yucheng Zhang, Kewei Gao and Guenter Schmitt
Publication Date: 2011
$0.00
$20.00
$20.00
Rotated cage corrosion experiments (4 m/s) were performed with flat coupons of 2 carbon steels (38Mn6/C75, X65) and 3 Cr-containing steels (X20Cr13, X2CrNiMoN22-5-3 (1.4462) and X1NiCrMoCu 25-20-5 (1.4539)) in the presence of supercritical carbon dioxide (scCO2) and different amounts of water at 50, 80, 110 and 130oC. While water-free scCO2 is non-corrosive for C-and Crcontaining steels, water mist saturated with scCO2 was corrosive for C-steels, however not for 13Cr or CrNi steels even up to 130°C. Droplets of water mist, saturated with scCO2, caused localized attack when touching the C-steel surface. Water phases saturated with scCO2 were very corrosive for C-steels in the whole range of 50 to 130°C (corrosion rates 5-15 mm/y and mesa-type localized attack). Under such conditions also the resistance of 13Cr steel was not acceptable (corrosion rates 0.3 to 0.8 mm/y). Even the austenitic-ferritic (1.4462) and the austenitic CrNi steel (1.4539) surpassed the target line of 0.1 mm/y at 110°C when contacted with water saturated with scCO2.

Keywords: carbon steels, 13 Cr steel, duplex steel, austenitic CrNi steel, water; corrosion, supercritical carbon dioxide, rotated cage,
Rotated cage corrosion experiments (4 m/s) were performed with flat coupons of 2 carbon steels (38Mn6/C75, X65) and 3 Cr-containing steels (X20Cr13, X2CrNiMoN22-5-3 (1.4462) and X1NiCrMoCu 25-20-5 (1.4539)) in the presence of supercritical carbon dioxide (scCO2) and different amounts of water at 50, 80, 110 and 130oC. While water-free scCO2 is non-corrosive for C-and Crcontaining steels, water mist saturated with scCO2 was corrosive for C-steels, however not for 13Cr or CrNi steels even up to 130°C. Droplets of water mist, saturated with scCO2, caused localized attack when touching the C-steel surface. Water phases saturated with scCO2 were very corrosive for C-steels in the whole range of 50 to 130°C (corrosion rates 5-15 mm/y and mesa-type localized attack). Under such conditions also the resistance of 13Cr steel was not acceptable (corrosion rates 0.3 to 0.8 mm/y). Even the austenitic-ferritic (1.4462) and the austenitic CrNi steel (1.4539) surpassed the target line of 0.1 mm/y at 110°C when contacted with water saturated with scCO2.

Keywords: carbon steels, 13 Cr steel, duplex steel, austenitic CrNi steel, water; corrosion, supercritical carbon dioxide, rotated cage,
Product tags
Also Purchased
Picture for 11377 Effect of Water Content on the Corrosion Behavior of Carbon Steel in Supercritical CO2 Phase
Available for download

11377 Effect of Water Content on the Corrosion Behavior of Carbon Steel in Supercritical CO2 Phase

Product Number: 51300-11377-SG
ISBN: 11377 2011 CP
Author: Yoon-Seok Choi and Srdjan Nesic
Publication Date: 2011
$20.00
Picture for 11379 Inhibition of Steel Corrosion Under Aqueous Supercritical CO2 Conditions
Available for download

11379 Inhibition of Steel Corrosion Under Aqueous Supercritical CO2 Conditions

Product Number: 51300-11379-SG
ISBN: 11379 2011 CP
Author: Yucheng Zhang, Kewei Gao and Guenter Schmitt
Publication Date: 2011
$20.00
Picture for 08430 Corrosion of Materials in Supercritical CO2 Environments
Available for download

08430 Corrosion of Materials in Supercritical CO2 Environments

Product Number: 51300-08430-SG
ISBN: 08430 2008 CP
Author: R. Ballinger, J. Lim, T. McKrell, and G. Eastwick
Publication Date: 2008
$20.00
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support