11262 Under-deposit Corrosion Failure of a Compressor after Stage Cooler at an NGL Plant- A Case Study

Picture for 11262 Under-Deposit Corrosion Failure of a Compressor
Available for download
Product Number: 51300-11262-SG
ISBN: 2011 11262 CP
Author: S. A. Al-Dossary, A. K. Debbert and M. A. Al- Mubayidh
Publication Date: 2011
$0.00
$20.00
$20.00
Premature tube leaks were encountered at a compressor after-stage cooler operating at 100-130?F (37.8-54.4?C) after three years in service due to under-deposit corrosion. The damage encountered was confirmed by visual, metallurgical examination and chemical analysis of corrosion products. The premature failure resulted from condensation of water containing dissolved carbon dioxide, hydrogen sulfide and possibly oxygen at the center bottom portion of the tube. Moreover, the presence of pitting in the liquid phase area indicates that the injection of the oil soluble water dispersible corrosion inhibitor was not effective. Chemical analysis of the deposits revealed that they comprised mainly of iron sulfide products. Metallurgical examination revealed no manufacturing defects. Corrective actions of similar failures are discussed in terms of design and inhibition.

Keywords: fin fan, corrosion inhibitor, hydrogen sulfide, failure analysis, Pourbaix diagram, mitigation
Premature tube leaks were encountered at a compressor after-stage cooler operating at 100-130?F (37.8-54.4?C) after three years in service due to under-deposit corrosion. The damage encountered was confirmed by visual, metallurgical examination and chemical analysis of corrosion products. The premature failure resulted from condensation of water containing dissolved carbon dioxide, hydrogen sulfide and possibly oxygen at the center bottom portion of the tube. Moreover, the presence of pitting in the liquid phase area indicates that the injection of the oil soluble water dispersible corrosion inhibitor was not effective. Chemical analysis of the deposits revealed that they comprised mainly of iron sulfide products. Metallurgical examination revealed no manufacturing defects. Corrective actions of similar failures are discussed in terms of design and inhibition.

Keywords: fin fan, corrosion inhibitor, hydrogen sulfide, failure analysis, Pourbaix diagram, mitigation
Product tags
Also Purchased
Picture for Under-Deposit Corrosion in a Sub-Sea Water Injection Pipeline—A Case Study
Available for download

Under-Deposit Corrosion in a Sub-Sea Water Injection Pipeline—A Case Study

Product Number: 51317--8973-SG
ISBN: 8973 2017 CP
Author: Pavan Shukla
Publication Date: 2017
$20.00

This paper pertains to a study of an API 5L X-60, Carbon steel, injection water pipeline, which failed prematurely in 4 years after commissioning due to under-deposit corrosion. A detailed study was carried out to investigate the failure causes.

 
Picture for 11266 Under Deposit Corrosion From Iron Sulfide
Available for download

11266 Under Deposit Corrosion From Iron Sulfide

Product Number: 51300-11266-SG
ISBN: 2011 11266 CP
Author: Sarah Standlee, K. Daniel Efird, Derek Spiller
Publication Date: 2011
$20.00
Picture for 05288 Test Methodologies and Field Verification of
Available for download

05288 Test Methodologies and Field Verification of Corrosion Inhibitors to Address under Deposit Corrosion in Oil and Gas Production Systems

Product Number: 51300-05288-SG
ISBN: 05288 2005 CP
Author: Han De Reus, Edwin L.J.A. Hendriksen, and Marc Wilms, Shell Global Solutions International; Yahya N.
$20.00
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support