10394 Corrosion of a Steel-Hulled Vessel by Cathodic Protecction

Picture for 10394 Corrosion of a Steel-Hulled Vessel by Cathodic Protecction
Available for download
Product Number: 51300-10394-SG
ISBN: 10394 2010 CP
Author: Derek R. Lenard
Publication Date: 2010
$0.00
$20.00
$20.00
A steel-hulled vessel was found to have suffered serious corrosion damage near one of its impressed current cathodic protection anodes. The damage was observed at breaks in the anode shield near a weld and in the cofferdam housing the anode. Underwater inspections revealed that all of the vessels in this class were experiencing similar problems. Several potential causes, such as the reversal of the power supply leads, were ruled out, as the cathodic protection system appeared to be functioning as designed. As a result, a theory was developed that involved an unusual corrosion mechanism that was dependent on the accumulation of alkaline by-products of the cathodic reaction, in conjunction with an overly “protective” potential. Laboratory simulations using potentiostatic techniques were performed in order to test this theory. Corrosion of the steel was observed within three days at a nominally “protective” potential.

Keywords: corrosion, cathodic protection, steel, seawater, potentiostatic polarization
A steel-hulled vessel was found to have suffered serious corrosion damage near one of its impressed current cathodic protection anodes. The damage was observed at breaks in the anode shield near a weld and in the cofferdam housing the anode. Underwater inspections revealed that all of the vessels in this class were experiencing similar problems. Several potential causes, such as the reversal of the power supply leads, were ruled out, as the cathodic protection system appeared to be functioning as designed. As a result, a theory was developed that involved an unusual corrosion mechanism that was dependent on the accumulation of alkaline by-products of the cathodic reaction, in conjunction with an overly “protective” potential. Laboratory simulations using potentiostatic techniques were performed in order to test this theory. Corrosion of the steel was observed within three days at a nominally “protective” potential.

Keywords: corrosion, cathodic protection, steel, seawater, potentiostatic polarization
Product tags
Also Purchased
Picture for 10404 Protection Against Microbiologically Influenced Corrosion by Effective Treatment
Available for download

10404 Protection Against Microbiologically Influenced Corrosion by Effective Treatment and Monitoring During Hydrotest Shut-In

Product Number: 51300-10404-SG
ISBN: 10404 2010 CP
Author: Joseph E. Penkala, Jennifer Fichter, and
Publication Date: 2010
$20.00
Picture for Penetration of Cathodic Protection into Pipeline Coating Disbondment
Available for download

Penetration of Cathodic Protection into Pipeline Coating Disbondment

Product Number: 51317--9146-SG
ISBN: 9146 2017 CP
Author: Li Yan
Publication Date: 2017
$20.00

An experimental setup was designed to investigate the cathodic protection (CP) penetration into coating disbondment. Embedded detection probes underneath the disbondment enabled pH and steel potential measurements without disturbing the environment inside the disbondment.
Picture for 10390 Design Validation of ICCP Systems for Offshore Wind Farms
Available for download

10390 Design Validation of ICCP Systems for Offshore Wind Farms

Product Number: 51300-10390-SG
ISBN: 10390 2010 CP
Author: Leslie Bortels, Jacques Parlongue, Joop de Leeuw and Bart Wessels
Publication Date: 2010
$20.00
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support