10317 Corrosion Performance of Alloy 29 in Simulated Sour Environments

Picture for 10317 Corrosion Performance of Alloy 29 in Simulated Sour Environments
Available for download
Product Number: 51300-10317-SG
ISBN: 10317 2010 CP
Author: Katarina B. Persson, Shamus J. Kaukas and Ulf H. Kivisäkk
Publication Date: 2010
$0.00
$20.00
$20.00
In order to evaluate the corrosion resistance of Alloy 29 material in sour environments, laboratory testing has been conducted using tensile test specimens. Testing was performed in accordance with NACE TM0177 Method A, modified for autoclave testing at high pressures and temperatures. The testing was performed at various temperatures, partial pressures of H2S and chloride concentrations of the brine. Considerably higher chloride concentration and partial pressure of H2S were used than what has previously been reported for this material. The tests were carried out both with and without elemental sulfur added to the brine. The results presented in this study suggest that the existing limits of 4c materials in the NACE standard MR0175/ ISO 15156 are too conservative for Alloy 29.

Keywords: Alloy 29, Sour service, Stress corrosion cracking, Hydrogen Sulfide, Elemental Sulfur
In order to evaluate the corrosion resistance of Alloy 29 material in sour environments, laboratory testing has been conducted using tensile test specimens. Testing was performed in accordance with NACE TM0177 Method A, modified for autoclave testing at high pressures and temperatures. The testing was performed at various temperatures, partial pressures of H2S and chloride concentrations of the brine. Considerably higher chloride concentration and partial pressure of H2S were used than what has previously been reported for this material. The tests were carried out both with and without elemental sulfur added to the brine. The results presented in this study suggest that the existing limits of 4c materials in the NACE standard MR0175/ ISO 15156 are too conservative for Alloy 29.

Keywords: Alloy 29, Sour service, Stress corrosion cracking, Hydrogen Sulfide, Elemental Sulfur
Product tags
Also Purchased
Picture for 10287 Critical Stress Corrosion Cracking Potentials of Stainless Steels in Dilute Chloride Solutions
Available for download

10287 Critical Stress Corrosion Cracking Potentials of Stainless Steels in Dilute Chloride Solutions

Product Number: 51300-10287-SG
ISBN: 10287 2010 CP
Author: Janardhan Rao Saithala, Steve McCoy, John Atkinson and Harvindher Singh Ubhi
Publication Date: 2010
$20.00
Picture for 10315 DCB Testing of C110 Material in Standard and Mild Sour Test Conditions
Available for download

10315 DCB Testing of C110 Material in Standard and Mild Sour Test Conditions

Product Number: 51300-10315-SG
ISBN: 10315 2010 CP
Author: C. Bosch, E. Wanzenberg, A.Gateaud, H. Marchebois, L. Delattre, R. Cury and C. Linne
Publication Date: 2010
$20.00
Picture for 10303 The Effect of Sensitization of Stress Corrosion Cracking of AA5083
Available for download

10303 The Effect of Sensitization of Stress Corrosion Cracking of AA5083

Product Number: 51300-10303-SG
ISBN: 10303 2010 CP
Author: Jie Gao and David J. Quesnel
Publication Date: 2010
$20.00
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support