10273 Erosion Corrosion of SS316L Trays in FCC's Sour Water Stripper

Picture for 10273 Erosion Corrosion of SS316L Trays in FCC's Sour Water Stripper
Available for download
Product Number: 51300-10273-SG
ISBN: 10273 2010 CP
Author: Saad Al-Dhafiri, Deepak Rawtal & Laxma Reddy
Publication Date: 2010
$0.00
$20.00
$20.00
FCC Sour Water Treatment Unit (with Side Reflux type) having design capacity of 22.7m³/hr. was commissioned in 1987. Ever since the increase in throughput of sour water in 1998, the Stripper experienced repeated failure of top trays made of SS316L in year 2004 (after in service for 17 years) and subsequently in 2008 & 2009. This paper deals with the failure investigation and root cause analysis of repeated failure of top three trays of Sour water stripper(V-95-101). Optical Microscopy & Scanning Electron Microscopy (SEM) studies of failed sample were carried out. Root cause analysis have indicated that erosion - corrosion due to Ammonium bi-sulfide (NH4HS) in the presence of hostile environment of chloride & cyanide with increase in throughput are the contributing factors for the failure.

Remedial measures such as minor modification to the cold reflux piping, up gradation of metallurgy and increase in thickness of affected trays are also discussed in the paper.

Keywords: FCC Sour water stripper, Erosion - corrosion, Ammonium bi-sulfide, Root cause analysis, SS316L trays
FCC Sour Water Treatment Unit (with Side Reflux type) having design capacity of 22.7m³/hr. was commissioned in 1987. Ever since the increase in throughput of sour water in 1998, the Stripper experienced repeated failure of top trays made of SS316L in year 2004 (after in service for 17 years) and subsequently in 2008 & 2009. This paper deals with the failure investigation and root cause analysis of repeated failure of top three trays of Sour water stripper(V-95-101). Optical Microscopy & Scanning Electron Microscopy (SEM) studies of failed sample were carried out. Root cause analysis have indicated that erosion - corrosion due to Ammonium bi-sulfide (NH4HS) in the presence of hostile environment of chloride & cyanide with increase in throughput are the contributing factors for the failure.

Remedial measures such as minor modification to the cold reflux piping, up gradation of metallurgy and increase in thickness of affected trays are also discussed in the paper.

Keywords: FCC Sour water stripper, Erosion - corrosion, Ammonium bi-sulfide, Root cause analysis, SS316L trays
Product tags
Also Purchased
Picture for 05569 The Application of Process Analyses to
Available for download

05569 The Application of Process Analyses to Prevent Corrosion in Sour Water Stripper Overhead Cooler Tubes

Product Number: 51300-05569-SG
ISBN: 05569 2005 CP
Author: Kazuhiro Toba and Koji Kawano, Idemitsu Engineering Company Ltd.; Koji Yamamoto and Yoshiaki Arakawa
$20.00
Picture for 10349 Prediction and Assessment of Ammonium Bisulfide Corrosion Under Refinery Sour Water
Available for download

10349 Prediction and Assessment of Ammonium Bisulfide Corrosion Under Refinery Sour Water Service Conditions-Part 2

Product Number: 51300-10349-SG
ISBN: 10349 2010 CP
Author: Richard J. Horvath, Vishal V. Lagad, Sridhar Srinivasan and Russell D. Kane
Publication Date: 2010
$20.00

This Phase II work in NH3-dominated sour waters studied the impact of several process variables including NH4HS concentration, NH3 partial pressure, H2S partial pressure, temperature, cyanide concentration, and velocity (wall shear stress).
Picture for 01531 METALLURGICAL EVALUATION OF A BULGED
Available for download

01531 METALLURGICAL EVALUATION OF A BULGED FCC REACTOR

Product Number: 51300-01531-SG
ISBN: 01531 2001 CP
Author: Gordon P. Kallenberg
$20.00
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support