10081 Recovery Boiler Superheater Corrosion Field Study

Picture for 10081 Recovery Boiler Superheater Corrosion Field Study
Available for download
Product Number: 51300-10081-SG
ISBN: 10081 2010 CP
Author: James R. Keiser, Joseph R. Kish, and Douglas L. Singbeil
Publication Date: 2010
$0.00
$20.00
$20.00
With the trend towards increasing the energy efficiency of black liquor recovery boilers in North America, there is a need to utilize superheater tubes with increased corrosion resistance that will permit operation at higher temperatures and pressures. In an effort to identify alloys with improved corrosion resistance under more harsh operating conditions, a field exposure was conducted that involved the insertion of an air-cooled probe, containing six candidate alloys, into the superheater section of an operating recovery boiler. A metallographic examination, complete with corrosion scale characterization using electron microprobe spectroscopy, was conducted after a 1,000 hour exposure period. Based on the results, a ranking of alloys based on corrosion performance was obtained.

Keywords: recovery boiler, black liquor, superheater, tube, corrosion, molten salt, chloride, sulfate, alloy
With the trend towards increasing the energy efficiency of black liquor recovery boilers in North America, there is a need to utilize superheater tubes with increased corrosion resistance that will permit operation at higher temperatures and pressures. In an effort to identify alloys with improved corrosion resistance under more harsh operating conditions, a field exposure was conducted that involved the insertion of an air-cooled probe, containing six candidate alloys, into the superheater section of an operating recovery boiler. A metallographic examination, complete with corrosion scale characterization using electron microprobe spectroscopy, was conducted after a 1,000 hour exposure period. Based on the results, a ranking of alloys based on corrosion performance was obtained.

Keywords: recovery boiler, black liquor, superheater, tube, corrosion, molten salt, chloride, sulfate, alloy
Product tags
Also Purchased
Picture for Recovery Boiler Tube Failure by Mechanisms of Stress-Assisted Corrosion and Phosphate Hideout
Available for download

Recovery Boiler Tube Failure by Mechanisms of Stress-Assisted Corrosion and Phosphate Hideout

Product Number: 51315-6059-SG
ISBN: 6059 2015 CP
Author: Max Moskal
Publication Date: 2015
$20.00

This paper presents an unusual case example of recovery boiler waterside tube deterioration by a combination of SAC and phosphate hideout corrosion mechanisms. The case shows boiler tubes that exhibited through-wall corrosion and cracking.
Picture for 08436 Boiler Tube Failures and Integrity Assessment
Available for download

08436 Boiler Tube Failures and Integrity Assessment

Product Number: 51300-08436-SG
ISBN: 08436 2008 CP
Author: Mohamed A. Saleem and Abdulwahab Hulaibi
Publication Date: 2008
$20.00
Picture for 96544 SOME COMMON CORROSION MECHANISMS LEADING
Available for download

96544 SOME COMMON CORROSION MECHANISMS LEADING TO BOILER TUBE FAILURE

Product Number: 51300-96544-SG
ISBN: 96544 1996 CP
Author: D. I. Bain, J. D. Haff, J. A. Kelly
$20.00
Categories
Industry
Recently viewed
Popular tags
View all

Association for Materials Protection and Performance

© AMPP All Rights Reserved.
Membership Terms of Content Use
Contact Customer Support